Investigation of properties of 5087aluminium alloy parts produced by Wire and Arc Additive Manufacturing
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F23%3A00371104" target="_blank" >RIV/68407700:21220/23:00371104 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Investigation of properties of 5087aluminium alloy parts produced by Wire and Arc Additive Manufacturing
Popis výsledku v původním jazyce
The paper deals with the influence of different arc modes within the cold metal transfer (CMT) process on the arc current and voltage waveforms and geometry of wire and arc additively manufactured (WAAM) AA5087 aluminium alloy single layer deposits. The arc modes included conventional cold metal transfer (CMT), CMT pulse (CMT-P), and CMT cycle step (CMT-CS). The results showed that various current and voltage waveforms characterized the different welding modes during the deposition process. The influence of welding mode on the cross-section of single-layer bead was evaluated. The largest width (8.2 mm) was measured for the CMT weld bead, followed by the CMT-CS (7.6 mm) and CMT-P bead (7.3 mm). The highest value of the bead height was observed for the weld bead produced by CMT mode (3.3 mm), followed by the weld bead fabricated by CMT-P and CMT-CS modes (2.9 mm).
Název v anglickém jazyce
Investigation of properties of 5087aluminium alloy parts produced by Wire and Arc Additive Manufacturing
Popis výsledku anglicky
The paper deals with the influence of different arc modes within the cold metal transfer (CMT) process on the arc current and voltage waveforms and geometry of wire and arc additively manufactured (WAAM) AA5087 aluminium alloy single layer deposits. The arc modes included conventional cold metal transfer (CMT), CMT pulse (CMT-P), and CMT cycle step (CMT-CS). The results showed that various current and voltage waveforms characterized the different welding modes during the deposition process. The influence of welding mode on the cross-section of single-layer bead was evaluated. The largest width (8.2 mm) was measured for the CMT weld bead, followed by the CMT-CS (7.6 mm) and CMT-P bead (7.3 mm). The highest value of the bead height was observed for the weld bead produced by CMT mode (3.3 mm), followed by the weld bead fabricated by CMT-P and CMT-CS modes (2.9 mm).
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20301 - Mechanical engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Technological forum 2023
ISBN
978-80-87583-40-1
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
292-297
Název nakladatele
Ing. Jan Kudláček
Místo vydání
Jaroměř
Místo konání akce
Hrubá Voda
Datum konání akce
27. 6. 2023
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—