Detailed Analysis of the Debris-Fretting Damage Areas on Coated Fuel Cladding

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F25%3A00378739" target="_blank" >RIV/68407700:21220/25:00378739 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.3390/ma18010143" target="_blank" >https://doi.org/10.3390/ma18010143</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma18010143" target="_blank" >10.3390/ma18010143</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Detailed Analysis of the Debris-Fretting Damage Areas on Coated Fuel Cladding

Popis výsledku v původním jazyce

Fuel failure caused by fretting damage to cladding remains a relevant issue, despite decades of research and development aimed at enhancing the physical parameters of fuel. This paper presents the results of experiments conducted at the Research Centre Řež on Zr-1%Nb alloy tube specimens covered with protective coatings made of chromium (Cr) and nitrogen (N) compounds. The experiments involved debris-fretting tests in dry conditions at room temperature, as well as microscopic measurements of groove depths. A detailed analysis was performed using Scanning Electron Microscopy, Energy-Dispersive X-ray Spectroscopy, and Focused Ion Beam techniques. The objectives of the tests were: (1) to compare the debris-fretting resistance between reference Zr-1%Nb specimens and those of the same alloy coated with various compositions, and (2) to demon-strate the positive effects of coating applications on the endurance of fuel cladding. The conducted analysis revealed a significant advantage in using cladding with a thin, wear-resistant layer compared to standard cladding material, with CrN-coated specimens exhibiting 36 times better fretting resistance.

Název v anglickém jazyce

Detailed Analysis of the Debris-Fretting Damage Areas on Coated Fuel Cladding

Popis výsledku anglicky

Fuel failure caused by fretting damage to cladding remains a relevant issue, despite decades of research and development aimed at enhancing the physical parameters of fuel. This paper presents the results of experiments conducted at the Research Centre Řež on Zr-1%Nb alloy tube specimens covered with protective coatings made of chromium (Cr) and nitrogen (N) compounds. The experiments involved debris-fretting tests in dry conditions at room temperature, as well as microscopic measurements of groove depths. A detailed analysis was performed using Scanning Electron Microscopy, Energy-Dispersive X-ray Spectroscopy, and Focused Ion Beam techniques. The objectives of the tests were: (1) to compare the debris-fretting resistance between reference Zr-1%Nb specimens and those of the same alloy coated with various compositions, and (2) to demon-strate the positive effects of coating applications on the endurance of fuel cladding. The conducted analysis revealed a significant advantage in using cladding with a thin, wear-resistant layer compared to standard cladding material, with CrN-coated specimens exhibiting 36 times better fretting resistance.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

1996-1944

Svazek periodika

18

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

001393759200001

EID výsledku v databázi Scopus

2-s2.0-85214525032