Influence of Artocarpus hirsutus (AH) cellulose micro fiber, bamboo fiber in thermoplastic biocomposites

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F25%3A00383323" target="_blank" >RIV/68407700:21220/25:00383323 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1038/s41598-025-88058-5" target="_blank" >https://doi.org/10.1038/s41598-025-88058-5</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1038/s41598-025-88058-5" target="_blank" >10.1038/s41598-025-88058-5</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Artocarpus hirsutus (AH) cellulose micro fiber, bamboo fiber in thermoplastic biocomposites

Popis výsledku v původním jazyce

In this experiment Artocarpus hirsutus (AH) fiber was utilized as the filler material for bamboo fiber (NF)/polyethylene (PE) biocomposites. This was a waste to wealth approach by utilising biomaterial and also can reduce the use of PE plastics. The crystallinity index (Crl) of 45.1%, 56.4%, 67% was observed in AH, alkali treated (NaOH) and cellulose AH fiber respectively. The combination with 20 wt% NF/3 wt% cellulose AH filler observed better tensile and flexural strength. Agglomeration at 4, 5 wt% affects the flexural properties by lesser interfacial adhesion with filler/matrix phase, having properties reducing up to 20.3 MPa. Comparing to cellulose AH filler, both alkali treated and untreated AH filler combinations possess lesser flexural strength. The addition of natural fibers increases the tensile and flexural modulus property with better properties at 30 wt% NF/5 wt% cellulose AH filler combination. The Impact strength doesn't observe high influence with filler incorporation. This AH fiber hasn't been explored in detail for mechanical and hydrophilic properties with incorporation with PE matrix. This fabricated composite is suited for bioengineering applications.

Název v anglickém jazyce

Influence of Artocarpus hirsutus (AH) cellulose micro fiber, bamboo fiber in thermoplastic biocomposites

Popis výsledku anglicky

In this experiment Artocarpus hirsutus (AH) fiber was utilized as the filler material for bamboo fiber (NF)/polyethylene (PE) biocomposites. This was a waste to wealth approach by utilising biomaterial and also can reduce the use of PE plastics. The crystallinity index (Crl) of 45.1%, 56.4%, 67% was observed in AH, alkali treated (NaOH) and cellulose AH fiber respectively. The combination with 20 wt% NF/3 wt% cellulose AH filler observed better tensile and flexural strength. Agglomeration at 4, 5 wt% affects the flexural properties by lesser interfacial adhesion with filler/matrix phase, having properties reducing up to 20.3 MPa. Comparing to cellulose AH filler, both alkali treated and untreated AH filler combinations possess lesser flexural strength. The addition of natural fibers increases the tensile and flexural modulus property with better properties at 30 wt% NF/5 wt% cellulose AH filler combination. The Impact strength doesn't observe high influence with filler incorporation. This AH fiber hasn't been explored in detail for mechanical and hydrophilic properties with incorporation with PE matrix. This fabricated composite is suited for bioengineering applications.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scientific Reports

ISSN

2045-2322

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

15

Strana od-do

1-15

Kód UT WoS článku

001416570900031

EID výsledku v databázi Scopus

2-s2.0-85218268433