Dielectric Properties of Plasma-sprayed Silicates

Popis výsledku v původním jazyce

Synthetic mullite, steatite and spodumene as well as natural olivine were plasma sprayed using water stabilized plasma system. The deposits were grounded and polished to produce samples in a shape of planparallel plates. These samples were then tested inAC field to measure their capacity and loss factor in frequency range from 200 Hz to 1MHz. Relative permittivity was calculated from the measured capacity. Volume resistivity was measured in DC field at voltage 100V. In addition dielectric strength of steatite was measured at 50Hz AC. It was shown that the relative permittivity of plasma sprayed silicates is less stable compared to bulk, in the whole studied frequency range.

Název v anglickém jazyce

Dielectric Properties of Plasma-sprayed Silicates

Popis výsledku anglicky

Synthetic mullite, steatite and spodumene as well as natural olivine were plasma sprayed using water stabilized plasma system. The deposits were grounded and polished to produce samples in a shape of planparallel plates. These samples were then tested inAC field to measure their capacity and loss factor in frequency range from 200 Hz to 1MHz. Relative permittivity was calculated from the measured capacity. Volume resistivity was measured in DC field at voltage 100V. In addition dielectric strength of steatite was measured at 50Hz AC. It was shown that the relative permittivity of plasma sprayed silicates is less stable compared to bulk, in the whole studied frequency range.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F03%2F0708" target="_blank" >GA202/03/0708: Difuzní koplanární výboje na povrchové úpravy polymerních materiálů a plazmové depozice za atmosférického tlaku</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

2005

Číslo periodika v rámci svazku

31

Stát vydavatele periodika

IT - Italská republika

Počet stran výsledku

7

Strana od-do

315-321

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—