Structure and Tribology of Biocompatible Ti-C:H Coatings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F07%3A00142349" target="_blank" >RIV/68407700:21230/07:00142349 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21220/07:00142349 RIV/68407700:21260/07:00142349

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure and Tribology of Biocompatible Ti-C:H Coatings

Popis výsledku v původním jazyce

Ti-C:H coatings with different carbon content for biomedical applications were deposited by PECVD. Ti was varied by magnetron sputtering a Ti-target with different power in a dc discharge regime having Ar in the atmosphere. The tribological properties were studied using a pin-on-disc CSM Tribometer in order to ensure stable tribological properties of the whole Ti-C:H/DLC system for any case of top layer failure. The sliding tests were carried out at room temperature in room environment with relative airhumidity 40+-5%, in 0.9% NaCl water solution (physiological solution, PS) and in 10% fetal bovine serum (FBS) dissolved in Ringer's saline solution using 440C steel balls with a diameter of 8 mm. The Ti-rich coatings exhibited poor wear resistance, while the best tribological properties were achieved for TiC/a-C:H coatings deposited with the highest C2H2 flows.

Název v anglickém jazyce

Structure and Tribology of Biocompatible Ti-C:H Coatings

Popis výsledku anglicky

Ti-C:H coatings with different carbon content for biomedical applications were deposited by PECVD. Ti was varied by magnetron sputtering a Ti-target with different power in a dc discharge regime having Ar in the atmosphere. The tribological properties were studied using a pin-on-disc CSM Tribometer in order to ensure stable tribological properties of the whole Ti-C:H/DLC system for any case of top layer failure. The sliding tests were carried out at room temperature in room environment with relative airhumidity 40+-5%, in 0.9% NaCl water solution (physiological solution, PS) and in 10% fetal bovine serum (FBS) dissolved in Ringer's saline solution using 440C steel balls with a diameter of 8 mm. The Ti-rich coatings exhibited poor wear resistance, while the best tribological properties were achieved for TiC/a-C:H coatings deposited with the highest C2H2 flows.

Druh

O - Ostatní výsledky

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů