High temperature tribology of CrN and multilayered Cr/CrN coatings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F09%3A00156125" target="_blank" >RIV/68407700:21230/09:00156125 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21110/09:00156125

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

High temperature tribology of CrN and multilayered Cr/CrN coatings

Popis výsledku v původním jazyce

Chromium nitride (CrN) and multilayers Cr/CrN coatings were deposited by low cathodic arc technology. The thickness of Cr and CrN layers was identical; two different multilayer coatings were deposited with layer thicknesses of 85 and 160 nm. The structural analysis showed that CrN coatings exhibited the cubic CrN phase, while a mixture of CrN, Cr2N and Cr phases was observed in the case of multilayers. The annealing of the samples at 800 and 900 °C in air led to: (1) the decomposition of the chromium nitride phases into chromium; (2) a moderate oxidation by forming a thin Cr2O3 layer on the coating surface and, (3) carbon diffusion from the steel substrate.

Název v anglickém jazyce

High temperature tribology of CrN and multilayered Cr/CrN coatings

Popis výsledku anglicky

Chromium nitride (CrN) and multilayers Cr/CrN coatings were deposited by low cathodic arc technology. The thickness of Cr and CrN layers was identical; two different multilayer coatings were deposited with layer thicknesses of 85 and 160 nm. The structural analysis showed that CrN coatings exhibited the cubic CrN phase, while a mixture of CrN, Cr2N and Cr phases was observed in the case of multilayers. The annealing of the samples at 800 and 900 °C in air led to: (1) the decomposition of the chromium nitride phases into chromium; (2) a moderate oxidation by forming a thin Cr2O3 layer on the coating surface and, (3) carbon diffusion from the steel substrate.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/KJB201240701" target="_blank" >KJB201240701: Nanokompozitní povlaky se zvýšenou otěruvzdorností za vyšších teplot</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Coatings Technology

ISSN

0257-8972

e-ISSN

—

Svazek periodika

203

Číslo periodika v rámci svazku

20-21

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000267632400043

EID výsledku v databázi Scopus

—