Spectroscopic and Dielectric Characterization of Plasma Sprayed Titanates

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F11%3A00183687" target="_blank" >RIV/68407700:21230/11:00183687 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61389021:_____/11:00365841

Výsledek na webu

<a href="http://www.intechopen.com/books/show/title/advances-in-ceramics-characterization-raw-materials-processing-properties-degradation" target="_blank" >http://www.intechopen.com/books/show/title/advances-in-ceramics-characterization-raw-materials-processing-properties-degradation</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Spectroscopic and Dielectric Characterization of Plasma Sprayed Titanates

Popis výsledku v původním jazyce

Raman and infrared spectroscopic measurements were carried out on plasma sprayed titanates CaTiO3, MgTiO3 and their mixture. Samples were tested in comparison with sintered analogs. Microwave microscopy was used for mapping of the dielectric response ofthe as-sprayed as well as annealed samples. The results show differences in the crystal lattice between plasma sprayed and sintered sample in the case of MgTiO3 whereas CaTiO3 is identical with its sintered bulk analog. The reason can be found in sensitivity of MgTiO3 to the reductive conditions at plasma spraying whereas CaTiO3 seems to be rather inert from this viewpoint.

Název v anglickém jazyce

Spectroscopic and Dielectric Characterization of Plasma Sprayed Titanates

Popis výsledku anglicky

Raman and infrared spectroscopic measurements were carried out on plasma sprayed titanates CaTiO3, MgTiO3 and their mixture. Samples were tested in comparison with sintered analogs. Microwave microscopy was used for mapping of the dielectric response ofthe as-sprayed as well as annealed samples. The results show differences in the crystal lattice between plasma sprayed and sintered sample in the case of MgTiO3 whereas CaTiO3 is identical with its sintered bulk analog. The reason can be found in sensitivity of MgTiO3 to the reductive conditions at plasma spraying whereas CaTiO3 seems to be rather inert from this viewpoint.

Druh

C - Kapitola v odborné knize

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Advances in Ceramics - Characterization, Raw Materials, Processing, Properties, Degradation and Healing

ISBN

978-953-307-504-4

Počet stran výsledku

20

Strana od-do

19-38

Počet stran knihy

370

Název nakladatele

InTech

Místo vydání

Rijeka

Kód UT WoS kapitoly

—