Temperature dependence of tribological properties of MoS2 and MoSe2 coatings

Popis výsledku v původním jazyce

This paper is aimed to the comparison of tribological properties of MoS2 and MoSe2 coatings measured in air of different humidity and at elevated temperatures. Both coatings were prepared by non-reactive DC magnetron sputtering and tested with ball-on-disc high temperature tribometer. The results of measurements of friction coefficient and wear rate vs. tribometer revolutions and the resulting dependencies of friction coefficient and wear rate on ambient air relative humidity are presented. These results show that the fiction coefficient of MoSe2 was not influenced by air humidity. Wear rate of MoSe2 in dry air was substantially higher than that of MoS2; in humid air, the MoS2 wear rate increased rapidly while wear rate of MoSe2 remained unchanged. Theoperating temperature of both coatings was limited to 350 degrees C.

Název v anglickém jazyce

Temperature dependence of tribological properties of MoS2 and MoSe2 coatings

Popis výsledku anglicky

This paper is aimed to the comparison of tribological properties of MoS2 and MoSe2 coatings measured in air of different humidity and at elevated temperatures. Both coatings were prepared by non-reactive DC magnetron sputtering and tested with ball-on-disc high temperature tribometer. The results of measurements of friction coefficient and wear rate vs. tribometer revolutions and the resulting dependencies of friction coefficient and wear rate on ambient air relative humidity are presented. These results show that the fiction coefficient of MoSe2 was not influenced by air humidity. Wear rate of MoSe2 in dry air was substantially higher than that of MoS2; in humid air, the MoS2 wear rate increased rapidly while wear rate of MoSe2 remained unchanged. Theoperating temperature of both coatings was limited to 350 degrees C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FD-K3%2F104" target="_blank" >FD-K3/104: Konsorcium pro výzkum a aplikace nanostrukturních povlaků zlepšujících tribologické vlastnosti strojních součástí. (Fakulta strojní)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Coatings Technology

ISSN

0257-8972

e-ISSN

—

Svazek periodika

193

Číslo periodika v rámci svazku

1-3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

230-233

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—