Srovnávací studie tribologického chování samomazných WSC a MoSeC vrstev

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21260%2F07%3A06139544" target="_blank" >RIV/68407700:21260/07:06139544 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Comparative Study of the Tribological Behaviour of Self-Lubricating W-S-C

Popis výsledku v původním jazyce

In this paper, the general comparison between W-S-C and Mo-Se-C coatings is presented. The main effort is pointed on the tribological behaviour of both systems when tested by pin-on-disk against steel counterpart balls under different testing conditions:applied normal loads, temperatures and relative humidity of the atmospheres. Both coatings were deposited by co-sputtering from a C target with a varying number of TMD pellets which could lead to C contents in the films in the range from 30 at.% up to 70 at.%. A Ti interlayer was interposed between the films and the substrates for improving the adhesion. Typically, W-S-C films are harder than Mo-Se-C films. From the tribological point of view, W-S-C films are more thermal stable than Mo-Se-C films although the friction coefficients of these last ones are lower when tested in humid containing atmospheres.

Název v anglickém jazyce

Comparative Study of the Tribological Behaviour of Self-Lubricating W-S-C

Popis výsledku anglicky

In this paper, the general comparison between W-S-C and Mo-Se-C coatings is presented. The main effort is pointed on the tribological behaviour of both systems when tested by pin-on-disk against steel counterpart balls under different testing conditions:applied normal loads, temperatures and relative humidity of the atmospheres. Both coatings were deposited by co-sputtering from a C target with a varying number of TMD pellets which could lead to C contents in the films in the range from 30 at.% up to 70 at.%. A Ti interlayer was interposed between the films and the substrates for improving the adhesion. Typically, W-S-C films are harder than Mo-Se-C films. From the tribological point of view, W-S-C films are more thermal stable than Mo-Se-C films although the friction coefficients of these last ones are lower when tested in humid containing atmospheres.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F07%2FP014" target="_blank" >GP106/07/P014: Samomazné vrstvy na bázi dichalkogenidů přechodových kovů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ECOTRIB 2007

ISBN

978-961-90254-8-2

ISSN

—

e-ISSN

—

Počet stran výsledku

11

Strana od-do

505-515

Název nakladatele

Slovenian Society for Tribology

Místo vydání

Ljubljana

Místo konání akce

Ljubljana

Datum konání akce

12. 6. 2007

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—