Mechanické a tribologické vlastnosti naprašovaných MoSeC povlaků.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21260%2F07%3A06139545" target="_blank" >RIV/68407700:21260/07:06139545 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical and Tribological Properties of Sputtered Mo-Se-C Coatings

Popis výsledku v původním jazyce

Mo Se C films were deposited by sputtering from a C target with pellets of MoSe2. Besides the evaluation of the chemical composition, the structure, the morphology, the hardness and the cohesion/adhesion, special attention was paid to the tribological characterization. The C content varied from 29 to 68 at.% which led to a progressive increase of the Se/Mo ratio. As a typical trend, the hardness increases with increasing C content. The coatings were tested at room temperature with different air humiditylevels and at temperatures up to 500 oC on a pin-on-disc tribometer. The friction coefficient of Mo-Se-C coatings increased with air humidity from ~0.04 to ~0.12, while it was as low as 0.02 at temperature range 100-250 oC. The coatings were very sensitive to the elevated temperature being worn out at 300 oC due to adhesion problems at coating - titanium interface.

Název v anglickém jazyce

Mechanical and Tribological Properties of Sputtered Mo-Se-C Coatings

Popis výsledku anglicky

Mo Se C films were deposited by sputtering from a C target with pellets of MoSe2. Besides the evaluation of the chemical composition, the structure, the morphology, the hardness and the cohesion/adhesion, special attention was paid to the tribological characterization. The C content varied from 29 to 68 at.% which led to a progressive increase of the Se/Mo ratio. As a typical trend, the hardness increases with increasing C content. The coatings were tested at room temperature with different air humiditylevels and at temperatures up to 500 oC on a pin-on-disc tribometer. The friction coefficient of Mo-Se-C coatings increased with air humidity from ~0.04 to ~0.12, while it was as low as 0.02 at temperature range 100-250 oC. The coatings were very sensitive to the elevated temperature being worn out at 300 oC due to adhesion problems at coating - titanium interface.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F07%2FP014" target="_blank" >GP106/07/P014: Samomazné vrstvy na bázi dichalkogenidů přechodových kovů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ECOTRIB 2007

ISBN

978-961-90254-8-2

ISSN

—

e-ISSN

—

Počet stran výsledku

11

Strana od-do

613-623

Název nakladatele

Slovenian Society for Tribology

Místo vydání

Ljubljana

Místo konání akce

Ljubljana

Datum konání akce

12. 6. 2007

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—