Příprava plechu ze slitiny AA 8006 s ultrajemnými zrny metodou ARB

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F04%3A04100018" target="_blank" >RIV/68407700:21340/04:04100018 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation of Ultra Fine Grain AA8006 Sheet by Accumulative Roll-Bonding

Popis výsledku v původním jazyce

Two pieces of the strip with dimensions of 250 mm x 50 mm x 2.5 mm were stacked to form a 5 mm thick specimen. Before stacking, the surfaces of the strips were degreased and wire-brushed to achieve good bonding. The pieces were joined together in the corners using Al wires and subsequently heated for 5 min to 200°C in an electrical furnace. After heating, the specimen was roll-bonded by rolling using a 50% reduction without lubricant. Five ARB cycles were successful. The initial material and the deformed microstructures were examined using electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM).

Název v anglickém jazyce

Preparation of Ultra Fine Grain AA8006 Sheet by Accumulative Roll-Bonding

Popis výsledku anglicky

Two pieces of the strip with dimensions of 250 mm x 50 mm x 2.5 mm were stacked to form a 5 mm thick specimen. Before stacking, the surfaces of the strips were degreased and wire-brushed to achieve good bonding. The pieces were joined together in the corners using Al wires and subsequently heated for 5 min to 200°C in an electrical furnace. After heating, the specimen was roll-bonded by rolling using a 50% reduction without lubricant. Five ARB cycles were successful. The initial material and the deformed microstructures were examined using electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM).

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of Workshop 2004

ISBN

80-01-02945-X

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

—

Název nakladatele

ČVUT

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

22. 3. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—