Luminescence Spectroscopy of Sn2P2S6 Crystals

Popis výsledku v původním jazyce

The emission and excitation spectra of luminescence of a Sn2P2S6 crystal were studied in detail within wide temperature (12 - 360 K) and spectral (260 - 1000 nm) regions. Illumination with monochromatic light with the wavelength shorter than about 710 nmat low temperatures enabled to observe broad-band photoluminescence in the red and near-infrared spectral regions. Analysis of the emission spectra revealed a superimposition of three overlapping bands peaking near 1.75, 1.57, and 1.39 eV at 12 K. At steady-state excitation at 12 K, the changes of photoluminescence intensity were observed with time of crystal illumination. During subsequent heating of the crystal with a rate of 0.082 K/s weak thermoluminescence was observed within 15 - 130 K. The trapdepths of 41 and 88 meV, corresponding to two pronounced glow peaks near 22 and 41 K, were determined by the "initial rise" method.

Název v anglickém jazyce

Luminescence Spectroscopy of Sn2P2S6 Crystals

Popis výsledku anglicky

The emission and excitation spectra of luminescence of a Sn2P2S6 crystal were studied in detail within wide temperature (12 - 360 K) and spectral (260 - 1000 nm) regions. Illumination with monochromatic light with the wavelength shorter than about 710 nmat low temperatures enabled to observe broad-band photoluminescence in the red and near-infrared spectral regions. Analysis of the emission spectra revealed a superimposition of three overlapping bands peaking near 1.75, 1.57, and 1.39 eV at 12 K. At steady-state excitation at 12 K, the changes of photoluminescence intensity were observed with time of crystal illumination. During subsequent heating of the crystal with a rate of 0.082 K/s weak thermoluminescence was observed within 15 - 130 K. The trapdepths of 41 and 88 meV, corresponding to two pronounced glow peaks near 22 and 41 K, were determined by the "initial rise" method.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GP202%2F02%2FD072" target="_blank" >GP202/02/D072: Optická spektroskopie dopovaných feroelektrických tenkých vrstev a krystalů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ferroelectrics

ISSN

0015-0193

e-ISSN

—

Svazek periodika

181-185

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

181-185

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—