Vliv vysokoteplotní degradace na šíření únavových trhlin v Cr-Mo ocelích používaných na výrobu potrubí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F05%3A04113296" target="_blank" >RIV/68407700:21340/05:04113296 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels

Popis výsledku v původním jazyce

In chemical and power engineering, tube systems are exposed to complex mechanical loading, high temperature, corrosion environment, etc. Long-time influence and interaction of severe conditions can result in the degradation of crucial properties of structural materials. Experimental research was aimed to the study of fatigue properties of three chrome-molybdenum steels: P91, ČSN 15 313 and N10 (21CrVMoW12). CT-specimens were cut out from thick-walled tubes. Materials of the tubes were tested in two different stages - original (without degradation), and degraded. Besides the material state and stress ratio, also orientation and location of specimens in the tube wall were under study, but the influence of these factors on fatigue crack growth was negligible. Fractographic analysis of the fatigued specimens was carried out.

Název v anglickém jazyce

Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels

Popis výsledku anglicky

In chemical and power engineering, tube systems are exposed to complex mechanical loading, high temperature, corrosion environment, etc. Long-time influence and interaction of severe conditions can result in the degradation of crucial properties of structural materials. Experimental research was aimed to the study of fatigue properties of three chrome-molybdenum steels: P91, ČSN 15 313 and N10 (21CrVMoW12). CT-specimens were cut out from thick-walled tubes. Materials of the tubes were tested in two different stages - original (without degradation), and degraded. Besides the material state and stress ratio, also orientation and location of specimens in the tube wall were under study, but the influence of these factors on fatigue crack growth was negligible. Fractographic analysis of the fatigued specimens was carried out.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of Workshop 2005 - Part A,B

ISBN

80-01-03201-9

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

458-459

Název nakladatele

ČVUT

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

21. 3. 2005

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—