Název v původním jazyce
Influence of Spraying Conditions on FatigueBehaviour of Hydroxyapatite Coatings
Popis výsledku v původním jazyce
Plasma spray deposition of low carbon steel specimens was carried out under three different conditions (denoted HA-1, HA-2, HA-3). To determine the influence of hydroxyapatite (HA) coatings on fatigue lives of machined low carbon steel specimens, fatigueexperiments using a symmetrical cyclical bending load were carried out. It was found out, all HA coatings led to prolongation of the fatigue lives as compared to specimens without coatings (by 43%, 23%, and 38%, respectively). Subsequent fractographic analysis confirmed that the fracture micromorphology of individual HA coatings is influenced by the different spraying conditions and fatigue cracks in coated bodies initiate underneath the coatings, i.e., on the steel substrate surface.
Název v anglickém jazyce
Influence of Spraying Conditions on FatigueBehaviour of Hydroxyapatite Coatings
Popis výsledku anglicky
Plasma spray deposition of low carbon steel specimens was carried out under three different conditions (denoted HA-1, HA-2, HA-3). To determine the influence of hydroxyapatite (HA) coatings on fatigue lives of machined low carbon steel specimens, fatigueexperiments using a symmetrical cyclical bending load were carried out. It was found out, all HA coatings led to prolongation of the fatigue lives as compared to specimens without coatings (by 43%, 23%, and 38%, respectively). Subsequent fractographic analysis confirmed that the fracture micromorphology of individual HA coatings is influenced by the different spraying conditions and fatigue cracks in coated bodies initiate underneath the coatings, i.e., on the steel substrate surface.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F05%2F0483" target="_blank" >GA106/05/0483: Vliv struktury na mechanické vlastnosti termicky deponovaných materiálů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Technica CSAV
ISSN
0001-7043
e-ISSN
—
Svazek periodika
52
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
11
Strana od-do
205-215
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—