Šíření únavových trhlin v austenitické oceli AISI 304L v primární vodě tlakovodního reaktoru při pokojové a zvýšené teplotě

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F07%3A04134913" target="_blank" >RIV/68407700:21340/07:04134913 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue Crack Growth in Austenitic Steel AISI 304L in PWR Primary Water at Room and Elevated Temperature

Popis výsledku v původním jazyce

Experimental work was focused to the study of fatigue crack growth behaviour of stainless austenitic steel AISI 304L at room and elevated temperature in water environment simulating exploitation conditions of nuclear power plants. For comparison, one setof CT specimens was tested in air at room temperature. The results of high cycle fatigue tests are presented in the form of macroscopic crack growth rate da/dN as a function of stress intensity factor range dK. Statistical processing of experimental data gives the best-fitted regression lines characterising reliably the fatigue properties of the steel under study and the influence of testing conditions. A detailed microfractographic analysis of specimen fractures extends information dealing with the influence of environment and temperature on fatigue fracture micromechanisms in the stage of macroscopic fatigue crack propagation.

Název v anglickém jazyce

Fatigue Crack Growth in Austenitic Steel AISI 304L in PWR Primary Water at Room and Elevated Temperature

Popis výsledku anglicky

Experimental work was focused to the study of fatigue crack growth behaviour of stainless austenitic steel AISI 304L at room and elevated temperature in water environment simulating exploitation conditions of nuclear power plants. For comparison, one setof CT specimens was tested in air at room temperature. The results of high cycle fatigue tests are presented in the form of macroscopic crack growth rate da/dN as a function of stress intensity factor range dK. Statistical processing of experimental data gives the best-fitted regression lines characterising reliably the fatigue properties of the steel under study and the influence of testing conditions. A detailed microfractographic analysis of specimen fractures extends information dealing with the influence of environment and temperature on fatigue fracture micromechanisms in the stage of macroscopic fatigue crack propagation.

Druh

C - Kapitola v odborné knize

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Corrosion Issues in Light Water Reactors. Stress Corrosion Cracking

ISBN

978-1-84569-242-1

Počet stran výsledku

10

Strana od-do

260-269

Počet stran knihy

—

Název nakladatele

Woodhead Publishing Ltd

Místo vydání

Cambridge

Kód UT WoS kapitoly

—