Fatigue and Fracture Toughness of Fe3Al Alloys with Additions of Zr and C
Popis výsledku v původním jazyce
Fracture behaviour of two intermetallic alloys based on Fe3Al with different Zr content was studied. On the alloy Fe-29.5Al-2.3Cr-0.63Zr-0.2C (at.%) (FA06Z), basic characterization of the microstructure by light and electron metallography was carried out. Tensile tests and fracture toughness tests were performed at 20, 200, 400, and 600°C. Previous fatigue experiments on the alloy Fe-31.5Al-3.5Cr-0.25Zr-0.2C (at.%) (FA02Z) were completed by fatigue tests at 150 and 600°C.
Název v anglickém jazyce
Fatigue and Fracture Toughness of Fe3Al Alloys with Additions of Zr and C
Popis výsledku anglicky
Fracture behaviour of two intermetallic alloys based on Fe3Al with different Zr content was studied. On the alloy Fe-29.5Al-2.3Cr-0.63Zr-0.2C (at.%) (FA06Z), basic characterization of the microstructure by light and electron metallography was carried out. Tensile tests and fracture toughness tests were performed at 20, 200, 400, and 600°C. Previous fatigue experiments on the alloy Fe-31.5Al-3.5Cr-0.25Zr-0.2C (at.%) (FA02Z) were completed by fatigue tests at 150 and 600°C.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—

Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)