Investigation of Correlations between Images of a Fracture Surface and Material Structure
Popis výsledku v původním jazyce
A specimen of welded joint in steam turbine was fractured by a fatigue crack. Fracture surface was documented by SEM, material microstructure by a light microscope. Fourier decomposition was used to image analysis. Three fatigue-independent characteristic dimensions were identified in fracture morphology. The substructure of martensitic laths was analyzed locally in 176 places. Two interpretations of mutual relations give significant agreement of characteristic dimensions in both sets of images.
Název v anglickém jazyce
Investigation of Correlations between Images of a Fracture Surface and Material Structure
Popis výsledku anglicky
A specimen of welded joint in steam turbine was fractured by a fatigue crack. Fracture surface was documented by SEM, material microstructure by a light microscope. Fourier decomposition was used to image analysis. Three fatigue-independent characteristic dimensions were identified in fracture morphology. The substructure of martensitic laths was analyzed locally in 176 places. Two interpretations of mutual relations give significant agreement of characteristic dimensions in both sets of images.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—

Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)