In-Situ Failure Observation of Thermal Spray Coatings

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F09%3A00160047" target="_blank" >RIV/68407700:21340/09:00160047 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
In-Situ Failure Observation of Thermal Spray Coatings
Popis výsledku v původním jazyce
Processes leading to the fracture of the coating are typically studied "post-mortem" by fractographic analysis of the fracture surfaces. Interpretation possibilities of the fractographic analysis can be extended when observing realtime microstructure changes in-situ or comparing changes before and after the failure. Specimens prepared from free-standing deposits of stainless steel 316 sprayed with water stabilized plasma (WSP) gun PAL 160 were loaded. Obtained micrographs enabled reconstruction of the crack growth within the coating.
Název v anglickém jazyce
In-Situ Failure Observation of Thermal Spray Coatings
Popis výsledku anglicky
Processes leading to the fracture of the coating are typically studied "post-mortem" by fractographic analysis of the fracture surfaces. Interpretation possibilities of the fractographic analysis can be extended when observing realtime microstructure changes in-situ or comparing changes before and after the failure. Specimens prepared from free-standing deposits of stainless steel 316 sprayed with water stabilized plasma (WSP) gun PAL 160 were loaded. Obtained micrographs enabled reconstruction of the crack growth within the coating.