Study of SrTiO3 Nanocrystalline Powder by Luminescent Impurity Probe Method
Popis výsledku v původním jazyce
Luminescence of Cr3+ impurity ions was used as a probe in studies of low-temperature phase of nanocrystalline SrTiO3:Cr(0.1%) powders with average particle size between 13 - 100 nm that were prepared by modified Pechini method. The temperature behavior of the zero-phonon emission R-line of the octahedral Cr3+ centres appeared for all powders nearly the same as that of the bulk crystals, evidencing that SrTiO3 retains quantum paraelectric behavior down to a particle size of about 10 nm.
Název v anglickém jazyce
Study of SrTiO3 Nanocrystalline Powder by Luminescent Impurity Probe Method
Popis výsledku anglicky
Luminescence of Cr3+ impurity ions was used as a probe in studies of low-temperature phase of nanocrystalline SrTiO3:Cr(0.1%) powders with average particle size between 13 - 100 nm that were prepared by modified Pechini method. The temperature behavior of the zero-phonon emission R-line of the octahedral Cr3+ centres appeared for all powders nearly the same as that of the bulk crystals, evidencing that SrTiO3 retains quantum paraelectric behavior down to a particle size of about 10 nm.

Projekt
<a href="/cs/project/GA202%2F08%2F1009" target="_blank" >GA202/08/1009: Charakterizace a technologie nových perovskitových struktur</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)