Mechanical Properties of Spark Plasma Sintered FeAl Intermetallics

Popis výsledku v původním jazyce

A recently developed powder metallurgy processing technique - Spark Plasma Sintering (SPS) was employed to produce specimens from gas atomized Fe-43at.%Al powder sieved into different size fractions. First, the sintering process parameters were optimised. When sintered under these optimised parameters, the different feedstock powder size fractions do not cause significant differences in microhardness and fracture toughness. Sintering temperatures below 950 °C are not sufficient to provide complete densification of the material. From the fractographic point of view, a change from interparticle decohesion to a mixture of interparticle decohesion and transgranular cleavage fracture with predominance of interparticle decohesion was observed with increasingsintering temperature from 950 to 1000 °C.

Název v anglickém jazyce

Mechanical Properties of Spark Plasma Sintered FeAl Intermetallics

Popis výsledku anglicky

A recently developed powder metallurgy processing technique - Spark Plasma Sintering (SPS) was employed to produce specimens from gas atomized Fe-43at.%Al powder sieved into different size fractions. First, the sintering process parameters were optimised. When sintered under these optimised parameters, the different feedstock powder size fractions do not cause significant differences in microhardness and fracture toughness. Sintering temperatures below 950 °C are not sufficient to provide complete densification of the material. From the fractographic point of view, a change from interparticle decohesion to a mixture of interparticle decohesion and transgranular cleavage fracture with predominance of interparticle decohesion was observed with increasingsintering temperature from 950 to 1000 °C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

18

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000279568600031

EID výsledku v databázi Scopus

—