Fatigue properties of Fe-Al intermetallic coatings prepared by plasma spraying
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F10%3A00173246" target="_blank" >RIV/68407700:21340/10:00173246 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389021:_____/10:00353721
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue properties of Fe-Al intermetallic coatings prepared by plasma spraying
Popis výsledku v původním jazyce
In this research, FeAl based coatings were deposited on low carbon steel using two different plasma spraying technologies - gas stabilized plasma gun (GSP) and water stabilized plasma gun (WSP) - resulting in different deposition conditions. Significantchanges in local chemical composition compared to feedstock material were observed due to uneven evaporation of Fe and Al from the molten material during the interaction of feedstock with plasma. Influence of coatings on substrate fatigue properties wascharacterized at room temperature using special testing device ''SF-Test''. Fatigue lifetimes of specimens with different coatings were compared with those of uncoated specimens. Fractographic analysis of failed specimens revealed that substrate fatiguecracks initiated at coating-substrate interface and grew by striation mechanism. The coatings failed due to intrasplat cracking and intersplat decohesion.
Název v anglickém jazyce
Fatigue properties of Fe-Al intermetallic coatings prepared by plasma spraying
Popis výsledku anglicky
In this research, FeAl based coatings were deposited on low carbon steel using two different plasma spraying technologies - gas stabilized plasma gun (GSP) and water stabilized plasma gun (WSP) - resulting in different deposition conditions. Significantchanges in local chemical composition compared to feedstock material were observed due to uneven evaporation of Fe and Al from the molten material during the interaction of feedstock with plasma. Influence of coatings on substrate fatigue properties wascharacterized at room temperature using special testing device ''SF-Test''. Fatigue lifetimes of specimens with different coatings were compared with those of uncoated specimens. Fractographic analysis of failed specimens revealed that substrate fatiguecracks initiated at coating-substrate interface and grew by striation mechanism. The coatings failed due to intrasplat cracking and intersplat decohesion.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ME%20901" target="_blank" >ME 901: Změny struktury a mechanických vlastností plazmových nástřiků při různém zatěžování</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Intermetallics
ISSN
0966-9795
e-ISSN
—
Svazek periodika
18
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000279568600032
EID výsledku v databázi Scopus
—