Stress Corrosion Cracking Testing in SCW - Results of SSRT Tests
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F11%3A00180255" target="_blank" >RIV/68407700:21340/11:00180255 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Stress Corrosion Cracking Testing in SCW - Results of SSRT Tests
Popis výsledku v původním jazyce
The presented paper summarizes the results of stress corrosion cracking (SCC) susceptibility tests in supercritical water (SCW) for austenitic alloys 316L, 316NG, 347HP and Alloy 690 with the aim to identify the maximum applicable SCW temperature and specific failure mechanisms prevailing during slow strain-rate tensile (SSRT) tests in ultra-pure demineralized SCW solution with controlled oxygen content. In addition to the strain rate, which was controlled by the crosshead speed, the oxygen content wasvaried in the series of tests in the case of austenitic stainless steel 316L. The fractography confirmed that failure was due to a combination of transgranular SCC and transgranular ductile fracture. Based on fractographic findings a phenomenological mapdescribing the SCC regime of SSRT test conditions was proposed for AISI 316L.
Název v anglickém jazyce
Stress Corrosion Cracking Testing in SCW - Results of SSRT Tests
Popis výsledku anglicky
The presented paper summarizes the results of stress corrosion cracking (SCC) susceptibility tests in supercritical water (SCW) for austenitic alloys 316L, 316NG, 347HP and Alloy 690 with the aim to identify the maximum applicable SCW temperature and specific failure mechanisms prevailing during slow strain-rate tensile (SSRT) tests in ultra-pure demineralized SCW solution with controlled oxygen content. In addition to the strain rate, which was controlled by the crosshead speed, the oxygen content wasvaried in the series of tests in the case of austenitic stainless steel 316L. The fractography confirmed that failure was due to a combination of transgranular SCC and transgranular ductile fracture. Based on fractographic findings a phenomenological mapdescribing the SCC regime of SSRT test conditions was proposed for AISI 316L.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
The 5th International Symposium on Supercritical-Water-Cooled Reactors
ISBN
978-1-926773-02-5
ISSN
—
e-ISSN
—
Počet stran výsledku
16
Strana od-do
"P32"
Název nakladatele
Canadian Nuclear Society
Místo vydání
Toronto
Místo konání akce
Vancouver
Datum konání akce
13. 3. 2011
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—