Characterization of Eu2O3 Nanolayers Deposited on Semiconductors

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F11%3A00190632" target="_blank" >RIV/68407700:21340/11:00190632 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of Eu2O3 Nanolayers Deposited on Semiconductors

Popis výsledku v původním jazyce

We report on the synthesis of europium oxide nanoparticles and the SEM characterization of europium oxide deposited on semiconductor wafers. The motivation is to prepare high quality nanolayers for Schottky diodes. Europium oxide thin film would be attractive for use in many nanoscale application i.e. ultraviolet-photoactive optical coating, electroluminescent display, and optical data storage. Europium oxide (Eu2O3) is the stable sesquioxide of the Eu3+ ion, which is exploited as a phosphorescence agent in light-emitting compounds. The optical properties of Eu2O3 originate from the Eu3+ ion absorption, whose primary fluorescent peak resides at 612nm. The core optical transitions are unaffected by the size or surface morphology of the materials. Europium oxides nanoparticles were prepared in colloids solution. A typical preparation is as follows; to the solution of europium chloride is added trioctyl phosphine oxide (TOPO) solution which is bound to the surface of nanoparticles. The pr

Název v anglickém jazyce

Characterization of Eu2O3 Nanolayers Deposited on Semiconductors

Popis výsledku anglicky

We report on the synthesis of europium oxide nanoparticles and the SEM characterization of europium oxide deposited on semiconductor wafers. The motivation is to prepare high quality nanolayers for Schottky diodes. Europium oxide thin film would be attractive for use in many nanoscale application i.e. ultraviolet-photoactive optical coating, electroluminescent display, and optical data storage. Europium oxide (Eu2O3) is the stable sesquioxide of the Eu3+ ion, which is exploited as a phosphorescence agent in light-emitting compounds. The optical properties of Eu2O3 originate from the Eu3+ ion absorption, whose primary fluorescent peak resides at 612nm. The core optical transitions are unaffected by the size or surface morphology of the materials. Europium oxides nanoparticles were prepared in colloids solution. A typical preparation is as follows; to the solution of europium chloride is added trioctyl phosphine oxide (TOPO) solution which is bound to the surface of nanoparticles. The pr

Druh

D - Stať ve sborníku

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2011 - Conference Proceedings

ISBN

978-80-87294-27-7

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

715-718

Název nakladatele

TANGER spol. s r.o.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 9. 2011

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—