Influence of Si and Fe on the distribution of intermetallic compounds in twin-roll cast Al-Mn-Zr alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F12%3A00186894" target="_blank" >RIV/68407700:21340/12:00186894 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jallcom.2011.11.101" target="_blank" >http://dx.doi.org/10.1016/j.jallcom.2011.11.101</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jallcom.2011.11.101" target="_blank" >10.1016/j.jallcom.2011.11.101</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Si and Fe on the distribution of intermetallic compounds in twin-roll cast Al-Mn-Zr alloys

Popis výsledku v původním jazyce

The aim of the experiments was to study the influence of Si and Fe on size and formation of secondary phases and recrystallization behaviour of Al-Mn-Zr alloys prepared by twin-roll casting (TRC) in the industrial conditions. A relatively high (0.5 wt.%)Si content and low (0.2 wt.%) Fe content in one of the alloys resulted in balancing of nucleation and dissolution rate for small particles. Hence a higher density of small particles was stable during the downstream processing, and this alloy showed improved recrystallization resistance.

Název v anglickém jazyce

Influence of Si and Fe on the distribution of intermetallic compounds in twin-roll cast Al-Mn-Zr alloys

Popis výsledku anglicky

The aim of the experiments was to study the influence of Si and Fe on size and formation of secondary phases and recrystallization behaviour of Al-Mn-Zr alloys prepared by twin-roll casting (TRC) in the industrial conditions. A relatively high (0.5 wt.%)Si content and low (0.2 wt.%) Fe content in one of the alloys resulted in balancing of nucleation and dissolution rate for small particles. Hence a higher density of small particles was stable during the downstream processing, and this alloy showed improved recrystallization resistance.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Alloys and Compounds

ISSN

0925-8388

e-ISSN

—

Svazek periodika

515

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

108-113

Kód UT WoS článku

000299105800022

EID výsledku v databázi Scopus

—