Residual stress depth profile in surface layers of shot-peened decarburized steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F12%3A00202909" target="_blank" >RIV/68407700:21340/12:00202909 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Residual stress depth profile in surface layers of shot-peened decarburized steels

Popis výsledku v původním jazyce

Surface decarburization of construction steels occurs during their forging, drawing and casting. As a softening process, decarburization leads to a considerable fatigue limit decrease. This detrimental effect can be reduced by strengthening the decarburized layer using plastic deformation induced by shot peening. As a result compressive residual stresses are created in the surface layer. The aim of the contribution is to present the results of X-ray diffraction analysis of residual stress depth profilesin surface layers of sand-blasted and shot-blasted steels. Depth distributions of macroscopic (first-order) residual stresses were determined up to approx. 500 ?m beneath the blasted surface.

Název v anglickém jazyce

Residual stress depth profile in surface layers of shot-peened decarburized steels

Popis výsledku anglicky

Surface decarburization of construction steels occurs during their forging, drawing and casting. As a softening process, decarburization leads to a considerable fatigue limit decrease. This detrimental effect can be reduced by strengthening the decarburized layer using plastic deformation induced by shot peening. As a result compressive residual stresses are created in the surface layer. The aim of the contribution is to present the results of X-ray diffraction analysis of residual stress depth profilesin surface layers of sand-blasted and shot-blasted steels. Depth distributions of macroscopic (first-order) residual stresses were determined up to approx. 500 ?m beneath the blasted surface.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI3%2F814" target="_blank" >FR-TI3/814: Optimalizace laserového povrchového zpracování strojních součástí pro zvýšení jejich užitných vlastností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the 50th Annual Conference on Experimental Stress Analysis

ISBN

978-80-01-05060-6

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

111-114

Název nakladatele

Czech Technical University in Prague

Místo vydání

Praha

Místo konání akce

Tábor

Datum konání akce

4. 6. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—