Fatigue Testing of TBC on Structural Steel by Cyclic Bending

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F15%3A00224054" target="_blank" >RIV/68407700:21340/15:00224054 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61389021:_____/15:00443554

Výsledek na webu

<a href="http://download.springer.com/static/pdf/621/art%253A10.1007%252Fs11666-014-0180-4.pdf?auth66=1421160497_4ad08ce962b2e057f0c0165720027d9b&ext=.pdf" target="_blank" >http://download.springer.com/static/pdf/621/art%253A10.1007%252Fs11666-014-0180-4.pdf?auth66=1421160497_4ad08ce962b2e057f0c0165720027d9b&ext=.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s11666-014-0180-4" target="_blank" >10.1007/s11666-014-0180-4</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue Testing of TBC on Structural Steel by Cyclic Bending

Popis výsledku v původním jazyce

For applications with variable loading, fatigue performance of coated parts is of utmost importance. In this study, fatigue performance of conventional structural steel coated with thermal barrier coating (TBC) was evaluated in cyclic bending mode by ``SF-Test?? device. Testing was carried out at each stage of the TBC preparation process, i.e., for as-received and grit-blasted substrates, as well as for samples with Ni-based bond-coat and complete TBC: bond-coat with YSZ-based top-coat. Comparison of results obtained for different loading amplitudes supplemented by fractographic analysis enabled identification of dominating failure mechanisms and demonstrated applicability of the high-frequency resonant bending test for evaluation of fatigue resistancealteration at each stage of the TBC deposition process.

Název v anglickém jazyce

Fatigue Testing of TBC on Structural Steel by Cyclic Bending

Popis výsledku anglicky

For applications with variable loading, fatigue performance of coated parts is of utmost importance. In this study, fatigue performance of conventional structural steel coated with thermal barrier coating (TBC) was evaluated in cyclic bending mode by ``SF-Test?? device. Testing was carried out at each stage of the TBC preparation process, i.e., for as-received and grit-blasted substrates, as well as for samples with Ni-based bond-coat and complete TBC: bond-coat with YSZ-based top-coat. Comparison of results obtained for different loading amplitudes supplemented by fractographic analysis enabled identification of dominating failure mechanisms and demonstrated applicability of the high-frequency resonant bending test for evaluation of fatigue resistancealteration at each stage of the TBC deposition process.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GPP108%2F12%2FP552" target="_blank" >GPP108/12/P552: Procesy porušování vrstvených materiálů v blízkosti fázových rozhraní</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Thermal Spray Technology

ISSN

1059-9630

e-ISSN

—

Svazek periodika

24

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

7

Strana od-do

168-174

Kód UT WoS článku

000347416800021

EID výsledku v databázi Scopus

2-s2.0-84925538441