Effect of compressive load on magnetic shape memory effect in Ni-Mn-Ga single crystal
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F15%3A00300643" target="_blank" >RIV/68407700:21340/15:00300643 - isvavai.cz</a>
Výsledek na webu
<a href="http://przyrbwn.icm.edu.pl/APP/PDF/128/a128z4p57.pdf" target="_blank" >http://przyrbwn.icm.edu.pl/APP/PDF/128/a128z4p57.pdf</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12693/APhysPolA.128.704" target="_blank" >10.12693/APhysPolA.128.704</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of compressive load on magnetic shape memory effect in Ni-Mn-Ga single crystal
Popis výsledku v původním jazyce
We investigated the effect of large compressive stress on magnetic shape memory effect in modulated 10M martensite of Ni-Mn-Ga Heusler alloy. The single crystalline sample deformed approximately elastically up to highest load 540 MPa. Structural and microstructural changes of a single crystal were analysed by X-ray diffraction 2D scan mapping in 2θ and ω. Although the crystal structure, lattice cell parameters, and twinned microstructure (a/b and modulation twinning) exhibited only small changes after the loading, the volume of the sample undergoing the magnetically induced reorientation decreased sharply while magnetic field necessary for the reorientation gradually increased. The extrapolation suggested that no magnetically induced reorientation might occur after compression of about 1 GPa.
Název v anglickém jazyce
Effect of compressive load on magnetic shape memory effect in Ni-Mn-Ga single crystal
Popis výsledku anglicky
We investigated the effect of large compressive stress on magnetic shape memory effect in modulated 10M martensite of Ni-Mn-Ga Heusler alloy. The single crystalline sample deformed approximately elastically up to highest load 540 MPa. Structural and microstructural changes of a single crystal were analysed by X-ray diffraction 2D scan mapping in 2θ and ω. Although the crystal structure, lattice cell parameters, and twinned microstructure (a/b and modulation twinning) exhibited only small changes after the loading, the volume of the sample undergoing the magnetically induced reorientation decreased sharply while magnetic field necessary for the reorientation gradually increased. The extrapolation suggested that no magnetically induced reorientation might occur after compression of about 1 GPa.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GB14-36566G" target="_blank" >GB14-36566G: Multidisciplinární výzkumné centrum moderních materiálů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Physica Polonica A
ISSN
0587-4246
e-ISSN
—
Svazek periodika
128
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
5
Strana od-do
704-708
Kód UT WoS článku
000366357300058
EID výsledku v databázi Scopus
—