Magnetic Properties of Ion Irradiated Fe75Mo8Cu1B16 Metallic Glass

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F17%3A00312424" target="_blank" >RIV/68407700:21340/17:00312424 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.12693/APhysPolA.131.768" target="_blank" >http://dx.doi.org/10.12693/APhysPolA.131.768</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.12693/APhysPolA.131.768" target="_blank" >10.12693/APhysPolA.131.768</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Magnetic Properties of Ion Irradiated Fe75Mo8Cu1B16 Metallic Glass

Popis výsledku v původním jazyce

Microstructure and thermomagnetic properties of ion-bombarded amorphous Fe75Mo8Cu1B16 alloy are investigated. The Mössbauer spectroscopy shows that surface regions at the air side of the ribbons irradiated with 2E16 ions/cm2 were significantly affected by 130 keV N+ ions. On the other hand, the opposite (wheel) side that was not exposed to ion irradiation is practically intact. The analysis of temperature dependences of magnetization shows the Curie points of 313 K and 316 K for as-quenched and irradiated samples, respectively. The maximum of magnetic entropy change calculated for the irradiated alloy in a magnetic field of 1.0 T occurs at 312.5 K and equals to 0.77 J/kg 1/K while that of the as-quenched sample is 0.74 J/kg 1/K.

Název v anglickém jazyce

Magnetic Properties of Ion Irradiated Fe75Mo8Cu1B16 Metallic Glass

Popis výsledku anglicky

Microstructure and thermomagnetic properties of ion-bombarded amorphous Fe75Mo8Cu1B16 alloy are investigated. The Mössbauer spectroscopy shows that surface regions at the air side of the ribbons irradiated with 2E16 ions/cm2 were significantly affected by 130 keV N+ ions. On the other hand, the opposite (wheel) side that was not exposed to ion irradiation is practically intact. The analysis of temperature dependences of magnetization shows the Curie points of 313 K and 316 K for as-quenched and irradiated samples, respectively. The maximum of magnetic entropy change calculated for the irradiated alloy in a magnetic field of 1.0 T occurs at 312.5 K and equals to 0.77 J/kg 1/K while that of the as-quenched sample is 0.74 J/kg 1/K.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

<a href="/cs/project/GA14-12449S" target="_blank" >GA14-12449S: Vliv radiace na vybrané fyzikální vlastnosti perspektivních slitin pro jaderná zařízení</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Physica Polonica A

ISSN

0587-4246

e-ISSN

1898-794X

Svazek periodika

131

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

3

Strana od-do

768-770

Kód UT WoS článku

000400907900053

EID výsledku v databázi Scopus

2-s2.0-85019612239