In-situ laser-ultrasonic characterization of austenite-martensite transformation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F17%3A00327210" target="_blank" >RIV/68407700:21340/17:00327210 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

In-situ laser-ultrasonic characterization of austenite-martensite transformation

Popis výsledku v původním jazyce

A novel method for in-situ characterization of structural processes in NiTi wires is proposed. This method is based on contactless generation and detection of longitudinal ultrasonic waves in a wire subjected to mechanical loadings; focused laser pulses are used for generation of the waves, a laser vibrometer is then used for their detection. The contact-less arrangement enables application of this method for a broad range of temperatures and loading modes. The method is utilized for characterization of stress-induced phases in a superelastic medical grade NiTi wire of the diameter 100 µm. The results show that the elastic moduli of the stress-induced martensite phase significantly depend on the temperature, exhibiting a more than 50 % decrease at elevated temperatures and at stress levels close to the plateau stress for the reverse transition. This indicates a structural instability on NiTi martensite under these conditions.

Název v anglickém jazyce

In-situ laser-ultrasonic characterization of austenite-martensite transformation

Popis výsledku anglicky

A novel method for in-situ characterization of structural processes in NiTi wires is proposed. This method is based on contactless generation and detection of longitudinal ultrasonic waves in a wire subjected to mechanical loadings; focused laser pulses are used for generation of the waves, a laser vibrometer is then used for their detection. The contact-less arrangement enables application of this method for a broad range of temperatures and loading modes. The method is utilized for characterization of stress-induced phases in a superelastic medical grade NiTi wire of the diameter 100 µm. The results show that the elastic moduli of the stress-induced martensite phase significantly depend on the temperature, exhibiting a more than 50 % decrease at elevated temperatures and at stress levels close to the plateau stress for the reverse transition. This indicates a structural instability on NiTi martensite under these conditions.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GB14-36566G" target="_blank" >GB14-36566G: Multidisciplinární výzkumné centrum moderních materiálů</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

SMART 2017

ISBN

978-84-946909-3-8

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

1538-1546

Název nakladatele

International Center for Numerical Methods in Engineering (CIMNE)

Místo vydání

Barcelona

Místo konání akce

Madrid

Datum konání akce

5. 6. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—