Temperature influence on spectroscopic and lasing properties of blue laser diode pumped Alexandrite crystal

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F18%3A00324037" target="_blank" >RIV/68407700:21340/18:00324037 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/18:00521865

Výsledek na webu

<a href="http://dx.doi.org/10.1117/12.2287787" target="_blank" >http://dx.doi.org/10.1117/12.2287787</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1117/12.2287787" target="_blank" >10.1117/12.2287787</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Temperature influence on spectroscopic and lasing properties of blue laser diode pumped Alexandrite crystal

Popis výsledku v původním jazyce

We report on influence of temperature on spectroscopic and lasing properties of Alexandrite (Cr3+:BeAl2O4) crystal. Fluorescence lifetime, polarization-resolved absorption and emission spectra, and laser characteristics at similar to 750 nm are described in detail within the 78-400 K temperature range. As a pumping source, 3.5 W InGaN blue laser-diode operating at 444 nm wavelength was used. The best results achieved were at similar to 353 K crystal temperature - 326 mW of continuous output power at 750 nm wavelength with the slope efficiency near 20% (related to absorbed pump power). At cryogenic temperatures, the Alexandrite laser generation at the so-called R-line, i.e not in the vibronic mode, has been observed.

Název v anglickém jazyce

Temperature influence on spectroscopic and lasing properties of blue laser diode pumped Alexandrite crystal

Popis výsledku anglicky

We report on influence of temperature on spectroscopic and lasing properties of Alexandrite (Cr3+:BeAl2O4) crystal. Fluorescence lifetime, polarization-resolved absorption and emission spectra, and laser characteristics at similar to 750 nm are described in detail within the 78-400 K temperature range. As a pumping source, 3.5 W InGaN blue laser-diode operating at 444 nm wavelength was used. The best results achieved were at similar to 353 K crystal temperature - 326 mW of continuous output power at 750 nm wavelength with the slope efficiency near 20% (related to absorbed pump power). At cryogenic temperatures, the Alexandrite laser generation at the so-called R-line, i.e not in the vibronic mode, has been observed.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20201 - Electrical and electronic engineering

Projekt

<a href="/cs/project/GA15-05360S" target="_blank" >GA15-05360S: Vliv teploty na spektroskopické a laserové vlastnosti pevnolátkových aktivních materiálů pro viditelnou až střední infračervenou oblast</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proc. SPIE 10511 Solid State Lasers XXVII: Technology and Devices

ISBN

978-1-5106-1507-6

ISSN

0277-786X

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

SPIE

Místo vydání

Bellingham

Místo konání akce

San Francisco

Datum konání akce

27. 1. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000432463600048