Technological aspects of Fe-Al-Si intermetallic alloy preparation by mechanical alloying

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F19%3A00332962" target="_blank" >RIV/68407700:21340/19:00332962 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.4028/www.scientific.net/KEM.810.101" target="_blank" >https://doi.org/10.4028/www.scientific.net/KEM.810.101</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.810.101" target="_blank" >10.4028/www.scientific.net/KEM.810.101</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Technological aspects of Fe-Al-Si intermetallic alloy preparation by mechanical alloying

Popis výsledku v původním jazyce

In this paper, recently developed ternary FeAl20Si20 (wt.%) alloy with promising high-temperature oxidation and wear resistance was prepared by mechanical alloying in a high-energy ball mill. The possibility to speed-up the mechanical alloying process by replacing aluminium (and partly silicon) elemental powder by the pre-alloyed powder (AlSi30) with relatively fine dispersion of Si in the Al-Si eutectic was examined. The microstructure, phase composition and mechanical properties after various time of mechanical alloying were characterized. The effect of using the pre-alloyed powders on kinetics of mechanical alloying is compared with the results obtained on batches prepared from elemental powders.

Název v anglickém jazyce

Technological aspects of Fe-Al-Si intermetallic alloy preparation by mechanical alloying

Popis výsledku anglicky

In this paper, recently developed ternary FeAl20Si20 (wt.%) alloy with promising high-temperature oxidation and wear resistance was prepared by mechanical alloying in a high-energy ball mill. The possibility to speed-up the mechanical alloying process by replacing aluminium (and partly silicon) elemental powder by the pre-alloyed powder (AlSi30) with relatively fine dispersion of Si in the Al-Si eutectic was examined. The microstructure, phase composition and mechanical properties after various time of mechanical alloying were characterized. The effect of using the pre-alloyed powders on kinetics of mechanical alloying is compared with the results obtained on batches prepared from elemental powders.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Key Engineering Materials

ISBN

978-3-0357-1447-0

ISSN

1013-9826

e-ISSN

—

Počet stran výsledku

6

Strana od-do

101-106

Název nakladatele

Trans Tech Publications Ltd

Místo vydání

Durnten-Zurich

Místo konání akce

Ostrava

Datum konání akce

10. 9. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—