Fe:CdMnTe Laser Generating 5.4 - 6 μm Radiation

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F19%3A00334016" target="_blank" >RIV/68407700:21340/19:00334016 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1117/12.2509387" target="_blank" >http://dx.doi.org/10.1117/12.2509387</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1117/12.2509387" target="_blank" >10.1117/12.2509387</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Fe:CdMnTe Laser Generating 5.4 - 6 μm Radiation
Popis výsledku v původním jazyce
Room temperature lasing of a set of Cd1-xMnxTe solid-solution crystals doped with Fe2+ ions was obtained under optical pumping by 4.1 µm liquid nitrogen cooled Fe2+:ZnSe laser. Oscillation wavelength maxima were found to increase linearly with Mn content x increase at a rate of about 60 nm per each 10 % of Mn content in the sample. The central oscillation wavelength as high as 5940 nm was obtained for sample with the highest Mn content (x=0.76). The output energy was found to decrease for samples with higher Mn content due to very strong non-radiative fluorescence quenching.
Název v anglickém jazyce
Fe:CdMnTe Laser Generating 5.4 - 6 μm Radiation
Popis výsledku anglicky
Room temperature lasing of a set of Cd1-xMnxTe solid-solution crystals doped with Fe2+ ions was obtained under optical pumping by 4.1 µm liquid nitrogen cooled Fe2+:ZnSe laser. Oscillation wavelength maxima were found to increase linearly with Mn content x increase at a rate of about 60 nm per each 10 % of Mn content in the sample. The central oscillation wavelength as high as 5940 nm was obtained for sample with the highest Mn content (x=0.76). The output energy was found to decrease for samples with higher Mn content due to very strong non-radiative fluorescence quenching.

Projekt
<a href="/cs/project/EF16_019%2F0000778" target="_blank" >EF16_019/0000778: Centrum pokročilých aplikovaných přírodních věd</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
Proc. SPIE 10896 Solid State Lasers XXVIII: Technology and Devices
ISBN
978-1-5106-2434-4
ISSN
0277-786X
e-ISSN
—
Počet stran výsledku
7
Strana od-do
—
Název nakladatele
SPIE
Místo vydání
Bellingham
Místo konání akce
San Francisco
Datum konání akce
2. 2. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000483062600042

Podobné výsledky(10)