Investigation of residual stresses in high-cycle loaded laser steel welds
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F19%3A00335788" target="_blank" >RIV/68407700:21340/19:00335788 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25797000:_____/19:N0000055
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Investigation of residual stresses in high-cycle loaded laser steel welds
Popis výsledku v původním jazyce
The paper contains results of a comprehensive experimental programme aimed at an evaluation of residual stresses in and near laser welds of pressure vessels steels using X-ray diffraction technique. Generally, the manufacturing processes of a machine component introduce residual stresses that have an important and may have even essential influence on their behaviour during service life. The goal of this contribution was to find the influence of high-cycle loading on the stresses´ relaxation in and near the welds. It has been found that the surface residual stress state is not the most important factor, either positive or negative, but the fatigue life more or less depends on the specific situation and condition of the materials and welds. On the other hand, the fatigue loading test caused the reduction of microdeformation values. The analysis of microstructure changes by X-ray diffraction could be an indicator of the future cracks initialization and their propagation.
Název v anglickém jazyce
Investigation of residual stresses in high-cycle loaded laser steel welds
Popis výsledku anglicky
The paper contains results of a comprehensive experimental programme aimed at an evaluation of residual stresses in and near laser welds of pressure vessels steels using X-ray diffraction technique. Generally, the manufacturing processes of a machine component introduce residual stresses that have an important and may have even essential influence on their behaviour during service life. The goal of this contribution was to find the influence of high-cycle loading on the stresses´ relaxation in and near the welds. It has been found that the surface residual stress state is not the most important factor, either positive or negative, but the fatigue life more or less depends on the specific situation and condition of the materials and welds. On the other hand, the fatigue loading test caused the reduction of microdeformation values. The analysis of microstructure changes by X-ray diffraction could be an indicator of the future cracks initialization and their propagation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10301 - Atomic, molecular and chemical physics (physics of atoms and molecules including collision, interaction with radiation, magnetic resonances, Mössbauer effect)
Návaznosti výsledku
Projekt
<a href="/cs/project/TH02010664" target="_blank" >TH02010664: Inovativní metody svařování vysokotlakých zařízení s využitím laserových technologií</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
EAN 2019 57th conference on experimental stress analysis CONFERENCE PROCEEDINGS
ISBN
9788021457669
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
24-29
Název nakladatele
Česká společnost pro mechaniku
Místo vydání
Praha
Místo konání akce
Luhačovice
Datum konání akce
3. 6. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—