INFLUENCE OF CORROSION OF BRASS METALIZED PLAIN STEEL BARS ON BOND STRENGTH WITH CONCRETE

Popis výsledku v původním jazyce

This paper evaluates the influence of thickness of metallized brass coating on bond strength of smooth bars in concrete. In the experiment, corrosion stability of the coating was evaluated considering the initial corrosion damage caused by alkali pore solution of fresh concrete. Bond strength was evaluated for both normal strength concrete (NSC) and ultra-high performance concrete (UHPC). Further, the corrosion attack on coating was studied microscopically and the relationship between its character and final bond strength was described. The results suggest that corrosion resistance of such coated reinforcement and its bond strength are related to the initial alkalinity of both fresh concretes and the additional alkalinity of UHPC. The results are discussed with regard to the trend of using dispersed steel concrete reinforcement coated with brass in high-performance composites.

Název v anglickém jazyce

INFLUENCE OF CORROSION OF BRASS METALIZED PLAIN STEEL BARS ON BOND STRENGTH WITH CONCRETE

Popis výsledku anglicky

This paper evaluates the influence of thickness of metallized brass coating on bond strength of smooth bars in concrete. In the experiment, corrosion stability of the coating was evaluated considering the initial corrosion damage caused by alkali pore solution of fresh concrete. Bond strength was evaluated for both normal strength concrete (NSC) and ultra-high performance concrete (UHPC). Further, the corrosion attack on coating was studied microscopically and the relationship between its character and final bond strength was described. The results suggest that corrosion resistance of such coated reinforcement and its bond strength are related to the initial alkalinity of both fresh concretes and the additional alkalinity of UHPC. The results are discussed with regard to the trend of using dispersed steel concrete reinforcement coated with brass in high-performance composites.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

C - Předmět řešení projektu podléhá obchodnímu tajemství (§ 504 Občanského zákoníku), ale název projektu, cíle projektu a u ukončeného nebo zastaveného projektu zhodnocení výsledku řešení projektu (údaje P03, P04, P15, P19, P29, PN8) dodané do CEP, jsou upraveny tak, aby byly zveřejnitelné.

Název statě ve sborníku

Book of Abstracts of 3rd International Symposium on Connections between Steel and Concrete

ISBN

978-3-945773-06-2

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

140-141

Název nakladatele

University of Stuttgart

Místo vydání

Stuttgart

Místo konání akce

Stuttgart

Datum konání akce

27. 9. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—