Ductile Fracture Pattern under Fatigue Conditions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21610%2F20%3A00345925" target="_blank" >RIV/68407700:21610/20:00345925 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Ductile Fracture Pattern under Fatigue Conditions

Popis výsledku v původním jazyce

Cyclic plasticity lies at the root of fatigue fracture in the ductile substances. Concurrently, plastic material models solving the total loading path are applying to computer processing very exacting, on the high numbers of load cycles. Consequently, for that end, in the treatise presented is introduced, in line with (Seiler, 2020), a model with especially small computational labor. It yields a macroscopic characterization of fatigue fracture by mixing the phase-field technique for brittle fracture with typical resistance interpretation. We obtain a local lifetime variable that depreciates the fracture durability gradually. When inferring the stress-strain path at the most, from cyclic material characteristic, only one increment per load cycle is needed. The version permits to depict fatigue crack initiation, growth and residual fracture.

Název v anglickém jazyce

Ductile Fracture Pattern under Fatigue Conditions

Popis výsledku anglicky

Cyclic plasticity lies at the root of fatigue fracture in the ductile substances. Concurrently, plastic material models solving the total loading path are applying to computer processing very exacting, on the high numbers of load cycles. Consequently, for that end, in the treatise presented is introduced, in line with (Seiler, 2020), a model with especially small computational labor. It yields a macroscopic characterization of fatigue fracture by mixing the phase-field technique for brittle fracture with typical resistance interpretation. We obtain a local lifetime variable that depreciates the fracture durability gradually. When inferring the stress-strain path at the most, from cyclic material characteristic, only one increment per load cycle is needed. The version permits to depict fatigue crack initiation, growth and residual fracture.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20102 - Construction engineering, Municipal and structural engineering

Projekt

<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Engineering Mechanics 2020: Book of full texts

ISBN

978-80-214-5896-3

ISSN

1805-8248

e-ISSN

—

Počet stran výsledku

4

Strana od-do

90-93

Název nakladatele

Institute of Thermomechanics, AS CR, v.v.i.

Místo vydání

Prague

Místo konání akce

Brno

Datum konání akce

24. 11. 2020

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—