Degradation of Colored Concrete Elements Due to Frost

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21610%2F22%3A00363433" target="_blank" >RIV/68407700:21610/22:00363433 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21450/22:00363433

Výsledek na webu

<a href="https://doi.org/10.4028/p-5ajm9a" target="_blank" >https://doi.org/10.4028/p-5ajm9a</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/p-5ajm9a" target="_blank" >10.4028/p-5ajm9a</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Degradation of Colored Concrete Elements Due to Frost

Popis výsledku v původním jazyce

This article is focused on changes in the properties of colored concrete due to frost. In contrast to conventional concrete structures, fair-faced concrete is exposed to external conditions and is therefore also prone to degradation of its surface. The durability of the surface layers is mainly reflected in the color saturation and resistance to mechanical damage. Therefore, the paper focuses on measuring the change in color and strength characteristics after 75 cycles of frost resistance. The measurement was performed on concrete samples colored with yellow, red and green powdered metal oxide-based pigments. Based on the results, we can concluded the frost resistance of colored concrete depends primarily on the type of pigment used.

Název v anglickém jazyce

Degradation of Colored Concrete Elements Due to Frost

Popis výsledku anglicky

This article is focused on changes in the properties of colored concrete due to frost. In contrast to conventional concrete structures, fair-faced concrete is exposed to external conditions and is therefore also prone to degradation of its surface. The durability of the surface layers is mainly reflected in the color saturation and resistance to mechanical damage. Therefore, the paper focuses on measuring the change in color and strength characteristics after 75 cycles of frost resistance. The measurement was performed on concrete samples colored with yellow, red and green powdered metal oxide-based pigments. Based on the results, we can concluded the frost resistance of colored concrete depends primarily on the type of pigment used.

Druh

C - Kapitola v odborné knize

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Materials and Technologies of Modern Production

ISBN

978-3-0364-1168-2

Počet stran výsledku

6

Strana od-do

191-196

Počet stran knihy

274

Název nakladatele

Trans Tech Publications Ltd.

Místo vydání

Pfaffikon

Kód UT WoS kapitoly

—