Assessment of Adhesion between Mineral Aggregate and Bituminous Binder using Digital Image Analysis

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21720%2F18%3A00333646" target="_blank" >RIV/68407700:21720/18:00333646 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21110/18:00330313 RIV/68407700:21720/18:00330313 RIV/68407700:21110/18:00333646

Výsledek na webu

<a href="http://dx.doi.org/10.14311/APP.2018.15.0126" target="_blank" >http://dx.doi.org/10.14311/APP.2018.15.0126</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.14311/APP.2018.15.0126" target="_blank" >10.14311/APP.2018.15.0126</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of Adhesion between Mineral Aggregate and Bituminous Binder using Digital Image Analysis

Popis výsledku v původním jazyce

This work presents how to assess a rate of adhesion between bituminous binder and mineral aggregate. Asphalt mixtures composed from grade bitumen 50/70, reference or modified with adhesion promoters based on amines, and aggregate (Brant, Zbraslav, Skuteč – 8-16 mm) were made and then photographed. Three adhesion assessment approaches were applied: (i) standardized adhesion visual assessment, (ii) gray level thresholding, and (iii) entropy-based image segmentation, both evaluated from digital images. It was shown that adhesion between both Brant and Skuteč and reference binder, expressed as a rate of binder-coated area onto aggregate particles, was equal to ca. 50-70 %, while mixture composed from Zbraslav exhibited ca. 70-80 %. If adhesion promoters were used, these areas increased in all three cases up to 80-90 %. It was shown that results obtained using visual and entropy segmentation analysis were very similar, while these differed in comparison with gray-level thresholding.

Název v anglickém jazyce

Assessment of Adhesion between Mineral Aggregate and Bituminous Binder using Digital Image Analysis

Popis výsledku anglicky

This work presents how to assess a rate of adhesion between bituminous binder and mineral aggregate. Asphalt mixtures composed from grade bitumen 50/70, reference or modified with adhesion promoters based on amines, and aggregate (Brant, Zbraslav, Skuteč – 8-16 mm) were made and then photographed. Three adhesion assessment approaches were applied: (i) standardized adhesion visual assessment, (ii) gray level thresholding, and (iii) entropy-based image segmentation, both evaluated from digital images. It was shown that adhesion between both Brant and Skuteč and reference binder, expressed as a rate of binder-coated area onto aggregate particles, was equal to ca. 50-70 %, while mixture composed from Zbraslav exhibited ca. 70-80 %. If adhesion promoters were used, these areas increased in all three cases up to 80-90 %. It was shown that results obtained using visual and entropy segmentation analysis were very similar, while these differed in comparison with gray-level thresholding.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA18-13830S" target="_blank" >GA18-13830S: Podrobný výzkum fyzikálně-chemické interakce a souvisejících jevů mezi asfaltem a kamenivem pomocí pokročilých experimentálních metod</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NMM 2018 - Nano & Macro Mechanics 2018

ISBN

978-80-01-06457-3

ISSN

—

e-ISSN

2336-5382

Počet stran výsledku

5

Strana od-do

126-130

Název nakladatele

Czech Technical University in Prague

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

20. 9. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000461834500023