Vytvrzování močovino formaldehydových adhesiv hydrolysátem kolagenního typu v kyselém prostředí
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F04%3A63502580" target="_blank" >RIV/70883521:28110/04:63502580 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Curing of Urea- formaldehyde Adhesives With Collagen Type Hydrolsates Under Acid Condition
Popis výsledku v původním jazyce
Condensation of dimethylol urea and its mixtures with urea or hydrolysate of chrome- tanned leather waste ( mass fraction in mixture 0.05) in presence of variable quantity of phtalic acid, as acid curing agent ( with mass fraction limits 0.01 - 0.1) wasstudied through TG technique. During condensation of sole dimethylol urea or its mixtures with urea, oxymethylene as well as methylene cross- links are produced at a ratio of approx. 1:1, presence of leather waste hydrolysate reduces this ratio to approx. 2:1 in favour of more stable methylene bridges. Higher concentration of phtalic acid ( above mass fraction 0.05) leads to formation of a new TG mass decrement wave in the 150 -180 oC temperature interval, which probably relates to transition of more unstable oxy-methylene bridges to more stable methylene bridges, with splitting off formadehyde. Oxy-methylene bridges may be regarded as a potential source of formaldehyde emissions by cured urea-formaldehyde adhesive films. Hydrolysates o
Název v anglickém jazyce
Curing of Urea- formaldehyde Adhesives With Collagen Type Hydrolsates Under Acid Condition
Popis výsledku anglicky
Condensation of dimethylol urea and its mixtures with urea or hydrolysate of chrome- tanned leather waste ( mass fraction in mixture 0.05) in presence of variable quantity of phtalic acid, as acid curing agent ( with mass fraction limits 0.01 - 0.1) wasstudied through TG technique. During condensation of sole dimethylol urea or its mixtures with urea, oxymethylene as well as methylene cross- links are produced at a ratio of approx. 1:1, presence of leather waste hydrolysate reduces this ratio to approx. 2:1 in favour of more stable methylene bridges. Higher concentration of phtalic acid ( above mass fraction 0.05) leads to formation of a new TG mass decrement wave in the 150 -180 oC temperature interval, which probably relates to transition of more unstable oxy-methylene bridges to more stable methylene bridges, with splitting off formadehyde. Oxy-methylene bridges may be regarded as a potential source of formaldehyde emissions by cured urea-formaldehyde adhesive films. Hydrolysates o
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CI - Průmyslová chemie a chemické inženýrství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Thermal Analysis and Calorimetry
ISSN
1418-2874
e-ISSN
—
Svazek periodika
—
Číslo periodika v rámci svazku
76
Stát vydavatele periodika
HU - Maďarsko
Počet stran výsledku
9
Strana od-do
1015-1023
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—