Vliv rychlosti chlazení na entalpickou a objemovou relaxaci polystyrenu
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F07%3A63505436" target="_blank" >RIV/70883521:28110/07:63505436 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/67985874:_____/07:00093742
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of cooling rate on enthalpy and volume relaxation of polystyrene
Popis výsledku v původním jazyce
This paper presents the results of measurements of physical aging on polystyrene with a narrow molecular weight distribution (Mw/Mn = 1.03). The evolution of the aging process was followed by recording the relaxed enthalpy and the accompanying decrease in volume, using differential scanning calorimetry and mercury-in-glass dilatometry, respectively. The measurements were carried out after cooling the sample at constant rate to the aging temperature. The cooling rate varied between 0.0037 and 1 °C/min. The aging data were fitted with the KWW and the TNM functions. The differences in the time scales of enthalpy, h, and volume, v, relaxation were relatively small. From the h(v) graphs the derivative dh/dv was found to amount to about 1.8 GPa, a value significantly exceeding the predictions of the thermodynamic model containing an additional internal variable.
Název v anglickém jazyce
Effect of cooling rate on enthalpy and volume relaxation of polystyrene
Popis výsledku anglicky
This paper presents the results of measurements of physical aging on polystyrene with a narrow molecular weight distribution (Mw/Mn = 1.03). The evolution of the aging process was followed by recording the relaxed enthalpy and the accompanying decrease in volume, using differential scanning calorimetry and mercury-in-glass dilatometry, respectively. The measurements were carried out after cooling the sample at constant rate to the aging temperature. The cooling rate varied between 0.0037 and 1 °C/min. The aging data were fitted with the KWW and the TNM functions. The differences in the time scales of enthalpy, h, and volume, v, relaxation were relatively small. From the h(v) graphs the derivative dh/dv was found to amount to about 1.8 GPa, a value significantly exceeding the predictions of the thermodynamic model containing an additional internal variable.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/IAA2060401" target="_blank" >IAA2060401: Vliv vnitřního tlaku na termomechanické vlastnosti polymerů při fyzikálním stárnutí</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Non-Crystalline Solids
ISSN
0022-3093
e-ISSN
—
Svazek periodika
—
Číslo periodika v rámci svazku
353
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
11
Strana od-do
2681-2691
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—