Dynamic-Mechanical Properties of Filled Styrene-Butadiene Rubber Compounds: Comparison of Tensile and Shear Data

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F07%3A63505465" target="_blank" >RIV/70883521:28110/07:63505465 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Dynamic-Mechanical Properties of Filled Styrene-Butadiene Rubber Compounds: Comparison of Tensile and Shear Data

Popis výsledku v původním jazyce

Most rubber articles are prepared from filler-elastomer compounds and dynamic mechanical data can give valuable insight into behaviour of such systems. The aim of this study was to compare complex tensile modulus E* and complex shear modulus G* using seven types of vulcanized filled rubbers and two testing devices. Carbon black and clay filled SBR compounds were tested. The tensile modulus E* was measured by Dynamic Mechanical Analyzer (DMA DX04T from R.M.I.) and the shear modulus G* by Rubber Process Analyzer (RPA 2000 from Alpha Technologies) at 1 Hz, 30°C and at small deformation amplitudes common to both devices. For characterization of tested materials we used absolute values of complex modulus E* and G* as well as values of loss factor tan . Thehighest values of /E*/, /G*/ and tan in tested carbon blacks were obtained for type N330. The highest values of /E*/, /G*/ and tan in tested clay fillers were found for organoclay Cloisite 93A. Maximum at the dependence tan /amplitude, ob

Název v anglickém jazyce

Dynamic-Mechanical Properties of Filled Styrene-Butadiene Rubber Compounds: Comparison of Tensile and Shear Data

Popis výsledku anglicky

Most rubber articles are prepared from filler-elastomer compounds and dynamic mechanical data can give valuable insight into behaviour of such systems. The aim of this study was to compare complex tensile modulus E* and complex shear modulus G* using seven types of vulcanized filled rubbers and two testing devices. Carbon black and clay filled SBR compounds were tested. The tensile modulus E* was measured by Dynamic Mechanical Analyzer (DMA DX04T from R.M.I.) and the shear modulus G* by Rubber Process Analyzer (RPA 2000 from Alpha Technologies) at 1 Hz, 30°C and at small deformation amplitudes common to both devices. For characterization of tested materials we used absolute values of complex modulus E* and G* as well as values of loss factor tan . Thehighest values of /E*/, /G*/ and tan in tested carbon blacks were obtained for type N330. The highest values of /E*/, /G*/ and tan in tested clay fillers were found for organoclay Cloisite 93A. Maximum at the dependence tan /amplitude, ob

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/FD-K3%2F043" target="_blank" >FD-K3/043: *Vývoj technologie tepelného a mechanického zpracování koalinu a lupku za účelem využití vzniklých materiálů v gumárenském a plastikářském průmyslu a v průmyslu stavebních hmot.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Polymers for Advanced Technologies

ISSN

1042-7147

e-ISSN

—

Svazek periodika

18

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—