Zvýšení krípové odolnosti v PS/MWCNT kompozitu připraveného mícháním v tavenině a srážením, nekovalentní funkcionalozace MWCNT

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F08%3A63507014" target="_blank" >RIV/70883521:28110/08:63507014 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Improved creep resistance in PS/MWNCNT composite fabricated by melt mixing or coagulation method; non-covalently functionalized MWCNT

Popis výsledku v původním jazyce

Polystyrene (PS)/multi-wall carbon nanotubes (MWCNT) nanocomposites were prepared by melt mixing in a co-rotating twin screw microcompounder and by coagulation method of PS/MWCNT sonicated dispersion in MEK poured into water. Before mixing and coagulation nanotubes of a commercial type of MWCNT were covered with PS nanospheres by microemulsion polymerization in order to increase their dispersibility and compatibility with composite matrix. Microemulsion polymerization was carried out under sonication inthe presence of surfactants (sodium dodecyl sulphate and amyl alcohol) and cross-linking agent (divinylbenzene). The structure of modified MWCNT revealed by SEM microscopy contains ca 30 nm nanospheres partially covering the nanotubes surface. The tensile creep properties of prepared composite were measured and compared with pure PS matrix. The effect of filler is much more pronounced in the case of composite prepared by coagulation. There was found significant increase in glass transit

Název v anglickém jazyce

Improved creep resistance in PS/MWNCNT composite fabricated by melt mixing or coagulation method; non-covalently functionalized MWCNT

Popis výsledku anglicky

Polystyrene (PS)/multi-wall carbon nanotubes (MWCNT) nanocomposites were prepared by melt mixing in a co-rotating twin screw microcompounder and by coagulation method of PS/MWCNT sonicated dispersion in MEK poured into water. Before mixing and coagulation nanotubes of a commercial type of MWCNT were covered with PS nanospheres by microemulsion polymerization in order to increase their dispersibility and compatibility with composite matrix. Microemulsion polymerization was carried out under sonication inthe presence of surfactants (sodium dodecyl sulphate and amyl alcohol) and cross-linking agent (divinylbenzene). The structure of modified MWCNT revealed by SEM microscopy contains ca 30 nm nanospheres partially covering the nanotubes surface. The tensile creep properties of prepared composite were measured and compared with pure PS matrix. The effect of filler is much more pronounced in the case of composite prepared by coagulation. There was found significant increase in glass transit

Druh

M - Uspořádání konference

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F06%2FP189" target="_blank" >GP106/06/P189: Adaptace vlastností polymerních nanokompozitů na bázi uhlíkových nanotrubic z pohledu teplotní stability</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Místo konání akce

Montpellier

Stát konání akce

FR - Francouzská republika

Datum zahájení akce

—

Datum ukončení akce

—

Celkový počet účastníků

1000

Počet zahraničních účastníků

995

Typ akce podle státní přísl. účastníků

WRD - Celosvětová akce