Syntéza a strukturní charakterizace nanokompozitů na bázi polyanilínu a mezoporézního uhlíku

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F08%3A63507025" target="_blank" >RIV/70883521:28110/08:63507025 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Synthesis and structural characterization of polyaniline/mesoporous carbon nanocomposite

Popis výsledku v původním jazyce

In this work, a new nanocomposite in which polyaniline (PANI) is encapsulated in ordered mesoporous carbon (CMK-3 type) has been synthesized. The aniline monomer was introduced into hosts from the vapor phase to avoid the formation of PANI layers on theouter surface. The structure and morphology of the nanocomposite were characterized by X-ray diffraction (XRD), N2 adsorption=desorption, FT-IR and Raman spectra, high-resolution transmission electron microscopy (HRTEM), and thermogravimetric analysis (TGA). The results show that PANI is almost formed in the channels of CMK-3 and the nanocomposite retains the ordered mesostructure. Encapsulated PANI exhibits better thermal stability than pure PANI because of confinement effect in the channel system. Theconductivity of PANI=CMK-3 nanocomposite containing 8.4 wt% PANI is 0.78 S=cm at room temperature.

Název v anglickém jazyce

Synthesis and structural characterization of polyaniline/mesoporous carbon nanocomposite

Popis výsledku anglicky

In this work, a new nanocomposite in which polyaniline (PANI) is encapsulated in ordered mesoporous carbon (CMK-3 type) has been synthesized. The aniline monomer was introduced into hosts from the vapor phase to avoid the formation of PANI layers on theouter surface. The structure and morphology of the nanocomposite were characterized by X-ray diffraction (XRD), N2 adsorption=desorption, FT-IR and Raman spectra, high-resolution transmission electron microscopy (HRTEM), and thermogravimetric analysis (TGA). The results show that PANI is almost formed in the channels of CMK-3 and the nanocomposite retains the ordered mesostructure. Encapsulated PANI exhibits better thermal stability than pure PANI because of confinement effect in the channel system. Theconductivity of PANI=CMK-3 nanocomposite containing 8.4 wt% PANI is 0.78 S=cm at room temperature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F06%2F0419" target="_blank" >GA202/06/0419: Tvorba elektrorheologických struktur a jejich charakterizace</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Polymer Analysis and Characterization

ISSN

1023-666X

e-ISSN

—

Svazek periodika

13

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

12

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—