Pressure-volume-temperature characteristics of cemented carbide feedstocks
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F10%3A63509287" target="_blank" >RIV/70883521:28110/10:63509287 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Pressure-volume-temperature characteristics of cemented carbide feedstocks
Popis výsledku v původním jazyce
Pressure-volume-temperature (PVT) characteristics of highly filled carbide powder compounds were investigated on high-pressure mercury dilatometer. The compounds containing cemented carbide powder and three components polymeric binder varied in the volume content of powder and the powder characteristics (particle size distribution and mean particle size). PVT data was found to be dependent on volume content (0-50 vol.%) of carbide powder in compounds; with increasing powder content, the discrepancies ina specific volume at applied pressure decreased, whereas melting temperatures remained unaffected as a polymeric binder was powder-filled (confirmed also with differential scanning calorimetry). Volumetric thermal expansion coefficient and compressibility were linearly and exponentially, respectively, dependent on presure. Further, studied carbide compounds showed weakly pornounced shifts in volumetric thermal expansion coefficients nad compressibility obtained for powders differing in
Název v anglickém jazyce
Pressure-volume-temperature characteristics of cemented carbide feedstocks
Popis výsledku anglicky
Pressure-volume-temperature (PVT) characteristics of highly filled carbide powder compounds were investigated on high-pressure mercury dilatometer. The compounds containing cemented carbide powder and three components polymeric binder varied in the volume content of powder and the powder characteristics (particle size distribution and mean particle size). PVT data was found to be dependent on volume content (0-50 vol.%) of carbide powder in compounds; with increasing powder content, the discrepancies ina specific volume at applied pressure decreased, whereas melting temperatures remained unaffected as a polymeric binder was powder-filled (confirmed also with differential scanning calorimetry). Volumetric thermal expansion coefficient and compressibility were linearly and exponentially, respectively, dependent on presure. Further, studied carbide compounds showed weakly pornounced shifts in volumetric thermal expansion coefficients nad compressibility obtained for powders differing in
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA103%2F08%2F1307" target="_blank" >GA103/08/1307: Reologické modelování toků polymerních materiálů za vysokých tlaků</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Latest Trends on Engineering Mechanics, Structures, Engineering Geology
ISBN
978-960-474-203-5
ISSN
—
e-ISSN
—
Počet stran výsledku
3
Strana od-do
—
Název nakladatele
WSEAS Press
Místo vydání
—
Místo konání akce
Corfu Island, Greece
Datum konání akce
1. 1. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—