Study of poly(1-butene) surface modified by air plasma treatment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F10%3A63509309" target="_blank" >RIV/70883521:28110/10:63509309 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Study of poly(1-butene) surface modified by air plasma treatment

Popis výsledku v původním jazyce

A low-temperature pulsed direct current discharge air plasma treatment has been used to improve the surface properties of poly(1-butene) films. The changes in the surface hydrophilicity and roughness of modified poly(l-butene) films were investigated bycontact angle measurements, scanning electron microscopy and atomic force microscopy. These experiments revealed that the plasma treatment can greatly change the surface chemistry as well as morphology of poly(l-butene). The polar functional groups generated due to plasma treatment on the surface of poly(l-butene) sheets causes decrease in contact angle. However, the aging process of the plasma treated samples showed that the effect was not permanent. Scanning electron microscope and atomic force microscope observations revealed that the surface topography was changed by air plasma etching, and the surface roughness increases.

Název v anglickém jazyce

Study of poly(1-butene) surface modified by air plasma treatment

Popis výsledku anglicky

A low-temperature pulsed direct current discharge air plasma treatment has been used to improve the surface properties of poly(1-butene) films. The changes in the surface hydrophilicity and roughness of modified poly(l-butene) films were investigated bycontact angle measurements, scanning electron microscopy and atomic force microscopy. These experiments revealed that the plasma treatment can greatly change the surface chemistry as well as morphology of poly(l-butene). The polar functional groups generated due to plasma treatment on the surface of poly(l-butene) sheets causes decrease in contact angle. However, the aging process of the plasma treated samples showed that the effect was not permanent. Scanning electron microscope and atomic force microscope observations revealed that the surface topography was changed by air plasma etching, and the surface roughness increases.

Druh

D - Stať ve sborníku

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ANTEC 2010 Plastics: Annual Technical Conference Proceedings

ISBN

978-0-9753707-8-0

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

Society of Plastics Engineers

Místo vydání

Dallas

Místo konání akce

Orlando

Datum konání akce

1. 1. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—