Phase separation, phase dissolution and crystallization in poly(e-caprolactone)/poly(styrene-co-acrylonitrile) blends

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F11%3A43865461" target="_blank" >RIV/70883521:28110/11:43865461 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Phase separation, phase dissolution and crystallization in poly(e-caprolactone)/poly(styrene-co-acrylonitrile) blends

Popis výsledku v původním jazyce

A blend of poly(e-caprolactone) (PCL) and poly(styrene-co-acrylonitrile) (SAN) containing 27.5 wt% of acrylonitrile having the critical composition (80/20 PCL/SAN) was studied. This PCL/SAN blend having a lower critical solution temperature (LCST) phaseboundary at 122°C offered an excellent opportunity to investigate, firstly the kinetics of phase separation above LCST (125-180°C), and secondly the kinetics of phase dissolution below LCST (50-115°C). The blend underwent a temperature-jump above LCST where spinodal decomposition (SD) proceeded, yielding a regularly phaseseparated structure (SD structure). Then, it was quenched to the temperatures below LCST when the phase dissolution proceeded. Optical microscopy was used to observe the spinodal decomposition qualitatively while light scattering was used to characterize the phase separation and phase dissolution quantitatively. It was found that during phase dissolution the peak maximum moved towards a smaller angle (wavelength of conc

Název v anglickém jazyce

Phase separation, phase dissolution and crystallization in poly(e-caprolactone)/poly(styrene-co-acrylonitrile) blends

Popis výsledku anglicky

A blend of poly(e-caprolactone) (PCL) and poly(styrene-co-acrylonitrile) (SAN) containing 27.5 wt% of acrylonitrile having the critical composition (80/20 PCL/SAN) was studied. This PCL/SAN blend having a lower critical solution temperature (LCST) phaseboundary at 122°C offered an excellent opportunity to investigate, firstly the kinetics of phase separation above LCST (125-180°C), and secondly the kinetics of phase dissolution below LCST (50-115°C). The blend underwent a temperature-jump above LCST where spinodal decomposition (SD) proceeded, yielding a regularly phaseseparated structure (SD structure). Then, it was quenched to the temperatures below LCST when the phase dissolution proceeded. Optical microscopy was used to observe the spinodal decomposition qualitatively while light scattering was used to characterize the phase separation and phase dissolution quantitatively. It was found that during phase dissolution the peak maximum moved towards a smaller angle (wavelength of conc

Druh

C - Kapitola v odborné knize

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/ED2.1.00%2F03.0111" target="_blank" >ED2.1.00/03.0111: Centrum polymerních systémů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Polymer Phase Behavior

ISBN

978-1-61324-336-7

Počet stran výsledku

29

Strana od-do

265-293

Počet stran knihy

316

Název nakladatele

Nova Science Publishers

Místo vydání

New York

Kód UT WoS kapitoly

—