Eletrorheological Properties of Suspensions of Polypyrrole Ribbon Particles in Silicone oil
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F11%3A43867256" target="_blank" >RIV/70883521:28110/11:43867256 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/70883521:28610/11:43867256
Výsledek na webu
<a href="http://dx.doi.org/10.1063/1.3604488" target="_blank" >http://dx.doi.org/10.1063/1.3604488</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1063/1.3604488" target="_blank" >10.1063/1.3604488</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Eletrorheological Properties of Suspensions of Polypyrrole Ribbon Particles in Silicone oil
Popis výsledku v původním jazyce
A new polypyrrole (PPy) ribbon particles structure has been synthesized by solution chemistry method (oxidative polymerization) in the presence of surfactant cetyltrimethylammonium bromide (CTAB) with oxidizing agent ammonium persulfate (APS). The resulted polymer was treated with ammonium hydroxide (NH4OH) several times to obtain different sample conductivity. PPy morphology was characterized by SEM. The suspensions were prepared by dispersing PPy with different conductivities in silicone oil. The electrorheological effect (ER) for the suspensions was examined under various electric fields using a rotational rheometer. It was found that suspension of only 3 wt. % of PPy ribbon particles showed large ER effect providing yield stress of 256 Pa at 3 kV.mm-1.
Název v anglickém jazyce
Eletrorheological Properties of Suspensions of Polypyrrole Ribbon Particles in Silicone oil
Popis výsledku anglicky
A new polypyrrole (PPy) ribbon particles structure has been synthesized by solution chemistry method (oxidative polymerization) in the presence of surfactant cetyltrimethylammonium bromide (CTAB) with oxidizing agent ammonium persulfate (APS). The resulted polymer was treated with ammonium hydroxide (NH4OH) several times to obtain different sample conductivity. PPy morphology was characterized by SEM. The suspensions were prepared by dispersing PPy with different conductivities in silicone oil. The electrorheological effect (ER) for the suspensions was examined under various electric fields using a rotational rheometer. It was found that suspension of only 3 wt. % of PPy ribbon particles showed large ER effect providing yield stress of 256 Pa at 3 kV.mm-1.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
AIP Conference Proceedings
ISSN
0094-243X
e-ISSN
—
Svazek periodika
1375
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
9
Strana od-do
275-283
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—