Natural weathering vs. accelerated UV radiation on mechanical properties in poly(1-butene)
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F11%3A43867280" target="_blank" >RIV/70883521:28110/11:43867280 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/70883521:28610/11:43867280
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Natural weathering vs. accelerated UV radiation on mechanical properties in poly(1-butene)
Popis výsledku v původním jazyce
The work directs attention towards the influence of natural weathering and accelerated UV degradation on resulting macroscopic properties in isotactic poly(1-butene) (PB-1). For this purpose, commercial-available PB-1 was extruded as tape. Two sets of prepared specimens were UV irradiated up to 300 hours and naturally weathered up to 103 days. Significant changes were consequently observed in evolution of mechanical properties where was observed a drop of tensile strength and elongation at break, whiletensile modulus shows different trend caused by phenomenon of chemicrystallization. Evolution of chemical species in specimens was observed using infrared spectroscopy and surface changes were observed by stereomicroscopy.
Název v anglickém jazyce
Natural weathering vs. accelerated UV radiation on mechanical properties in poly(1-butene)
Popis výsledku anglicky
The work directs attention towards the influence of natural weathering and accelerated UV degradation on resulting macroscopic properties in isotactic poly(1-butene) (PB-1). For this purpose, commercial-available PB-1 was extruded as tape. Two sets of prepared specimens were UV irradiated up to 300 hours and naturally weathered up to 103 days. Significant changes were consequently observed in evolution of mechanical properties where was observed a drop of tensile strength and elongation at break, whiletensile modulus shows different trend caused by phenomenon of chemicrystallization. Evolution of chemical species in specimens was observed using infrared spectroscopy and surface changes were observed by stereomicroscopy.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED2.1.00%2F03.0111" target="_blank" >ED2.1.00/03.0111: Centrum polymerních systémů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Annual Technical Conference - ANTEC, Conference Proceedings
ISBN
978-1-61782-960-4
ISSN
—
e-ISSN
—
Počet stran výsledku
3
Strana od-do
2278-2280
Název nakladatele
Society of Plastics Engineers, Inc.
Místo vydání
Brookfield
Místo konání akce
Boston
Datum konání akce
1. 5. 2011
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—