Ethylene-Octene Copolymers/Organoclay Nanocomposites: Preparation and Properties

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F16%3A43874346" target="_blank" >RIV/70883521:28110/16:43874346 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.hindawi.com/journals/jnm/2016/6014064/" target="_blank" >http://www.hindawi.com/journals/jnm/2016/6014064/</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1155/2016/6014064" target="_blank" >10.1155/2016/6014064</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Ethylene-Octene Copolymers/Organoclay Nanocomposites: Preparation and Properties

Popis výsledku v původním jazyce

Two ethylene-octene copolymers with 17 and 45 wt.% of octene (EOC-17 and EOC-45) were compared in nanocomposites with Cloisite 93A. EOC-45 nanocomposites have a higher elongation at break. Dynamical mechanical analysis (DMA) showed a decrease of tan δ with frequency for EOC-17 nanocomposites, but decrease is followed by an increase for EOC-45 nanocomposites; DMA showed also increased modulus for all nanocomposites compared to pure copolymers over a wide temperature range. Barrier properties were improved about 100% by addition of organoclay; they were better for EOC-17 nanocomposites due to higher crystallinity. X-ray diffraction (XRD) together with transmission electron microscopy (TEM) showed some intercalation for EOC-17 but much better dispersion for EOC-45 nanocomposites. Differential scanning calorimetry (DSC) showed increased crystallization temperature Tc for EOC-17 nanocomposite (aggregates acted as nucleation agents) but decrease Tc for EOC-45 nanocomposite together with greatly influenced melting peak. Accelerated UV aging showed smaller C=O peak for EOC-45 nanocomposites.

Název v anglickém jazyce

Ethylene-Octene Copolymers/Organoclay Nanocomposites: Preparation and Properties

Popis výsledku anglicky

Two ethylene-octene copolymers with 17 and 45 wt.% of octene (EOC-17 and EOC-45) were compared in nanocomposites with Cloisite 93A. EOC-45 nanocomposites have a higher elongation at break. Dynamical mechanical analysis (DMA) showed a decrease of tan δ with frequency for EOC-17 nanocomposites, but decrease is followed by an increase for EOC-45 nanocomposites; DMA showed also increased modulus for all nanocomposites compared to pure copolymers over a wide temperature range. Barrier properties were improved about 100% by addition of organoclay; they were better for EOC-17 nanocomposites due to higher crystallinity. X-ray diffraction (XRD) together with transmission electron microscopy (TEM) showed some intercalation for EOC-17 but much better dispersion for EOC-45 nanocomposites. Differential scanning calorimetry (DSC) showed increased crystallization temperature Tc for EOC-17 nanocomposite (aggregates acted as nucleation agents) but decrease Tc for EOC-45 nanocomposite together with greatly influenced melting peak. Accelerated UV aging showed smaller C=O peak for EOC-45 nanocomposites.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/TA03010799" target="_blank" >TA03010799: Využití nanomateriálů a přírodních extraktů jako funkčních látek ve vývoji aktivních obalových materiálů s bariérovým efektem, antimikrobiálním, protektivním a kyslík pohlcujícím efektem</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Nanomaterials

ISSN

1687-4110

e-ISSN

—

Svazek periodika

2016

Číslo periodika v rámci svazku

Neuveden

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

14

Strana od-do

—

Kód UT WoS článku

000369331100001

EID výsledku v databázi Scopus

2-s2.0-84958581082