The effect of carbon black loading on the intrinsic strength of rubber based on EPDM
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F17%3A63510507" target="_blank" >RIV/70883521:28110/17:63510507 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/70883521:28610/17:63510507
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of carbon black loading on the intrinsic strength of rubber based on EPDM
Popis výsledku v původním jazyce
The intrinsic strengths for ethylene propylene diene monomer rubber (EPDM), varied in carbon black type N330, N550 and in the volume 50, 70 and 90 phr have been compounded and evaluated. The measurement was based on quasi-static tension loading on an edge-cracked pure shear specimen, combined with frictionless cutting via a sharp blade. The cutting force and prestress parameters were varied automatically using the Intrinsic strength Analyzer (ISA©) instrument manufactured by Coesfeld GmbH. It was observed that the intrinsic cutting energy decreases with increase of carbon black content independent on its type, however the intrinsic cutting energy rapidly decrease with increase of carbon black particle diameter.
Název v anglickém jazyce
The effect of carbon black loading on the intrinsic strength of rubber based on EPDM
Popis výsledku anglicky
The intrinsic strengths for ethylene propylene diene monomer rubber (EPDM), varied in carbon black type N330, N550 and in the volume 50, 70 and 90 phr have been compounded and evaluated. The measurement was based on quasi-static tension loading on an edge-cracked pure shear specimen, combined with frictionless cutting via a sharp blade. The cutting force and prestress parameters were varied automatically using the Intrinsic strength Analyzer (ISA©) instrument manufactured by Coesfeld GmbH. It was observed that the intrinsic cutting energy decreases with increase of carbon black content independent on its type, however the intrinsic cutting energy rapidly decrease with increase of carbon black particle diameter.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10404 - Polymer science
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Librix.eu
ISBN
978-80-89841-04-2
ISSN
—
e-ISSN
neuvedeno
Počet stran výsledku
4
Strana od-do
68-71
Název nakladatele
PMA 2017, SRC 2017
Místo vydání
Bratislava
Místo konání akce
Bratislava
Datum konání akce
29. 5. 2017
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—