Comparative study of pvdf sheets and their sensitivity to mechanical vibrations: The role of dimensions, molecular weight, stretching and poling

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F21%3A63542658" target="_blank" >RIV/70883521:28110/21:63542658 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/70883521:28610/21:63542658 RIV/00216305:26220/21:PU141335

Výsledek na webu

<a href="https://www.mdpi.com/2079-4991/11/7/1637" target="_blank" >https://www.mdpi.com/2079-4991/11/7/1637</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/nano11071637" target="_blank" >10.3390/nano11071637</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Comparative study of pvdf sheets and their sensitivity to mechanical vibrations: The role of dimensions, molecular weight, stretching and poling

Popis výsledku v původním jazyce

This paper is focused on the comparative study of the vibration sensing capabilities of poly(vinylidene fluoride) (PVDF) sheets. The main parameters such as molecular weight, initial sample thickness, stretching and poling were systematically applied, and their impact on sensing behavior was examined. The mechanical properties of prepared sheets were investigated via tensile testing on the samples with various initial thicknesses. The transformation of the α-phase to the electro-active β-phase was analyzed using FTIR after applying stretching and poling procedures as crucial post-processing techniques. As a complementary method, the XRD was applied, and it confirmed the crystallinity data resulting from the FTIR analysis. The highest degree of phase transformation was found in the PVDF sheet with a moderate molecular weight (Mw of 275 kDa) after being subjected to the highest axial elongation (500%); in this case, the β-phase content reached approximately 90%. Finally, the vibration sensing capability was systematically determined, and all the mentioned processing/molecular parameters were taken into consideration. The whole range of the elongations (from 50 to 500%) applied on the PVDF sheets with an Mw of 180 and 275 kDa and an initial thickness of 0.5 mm appeared to be sufficient for vibration sensing purposes, showing a d33 piezoelectric charge coefficient from 7 pC N−1 to 9.9 pC N−1 . In terms of the d33, the PVDF sheets were suitable regardless of their Mw only after applying the elongation of 500%. Among all the investigated samples, those with an initial thickness of 1.0 mm did not seem to be suitable for vibration sensing purposes.

Název v anglickém jazyce

Comparative study of pvdf sheets and their sensitivity to mechanical vibrations: The role of dimensions, molecular weight, stretching and poling

Popis výsledku anglicky

This paper is focused on the comparative study of the vibration sensing capabilities of poly(vinylidene fluoride) (PVDF) sheets. The main parameters such as molecular weight, initial sample thickness, stretching and poling were systematically applied, and their impact on sensing behavior was examined. The mechanical properties of prepared sheets were investigated via tensile testing on the samples with various initial thicknesses. The transformation of the α-phase to the electro-active β-phase was analyzed using FTIR after applying stretching and poling procedures as crucial post-processing techniques. As a complementary method, the XRD was applied, and it confirmed the crystallinity data resulting from the FTIR analysis. The highest degree of phase transformation was found in the PVDF sheet with a moderate molecular weight (Mw of 275 kDa) after being subjected to the highest axial elongation (500%); in this case, the β-phase content reached approximately 90%. Finally, the vibration sensing capability was systematically determined, and all the mentioned processing/molecular parameters were taken into consideration. The whole range of the elongations (from 50 to 500%) applied on the PVDF sheets with an Mw of 180 and 275 kDa and an initial thickness of 0.5 mm appeared to be sufficient for vibration sensing purposes, showing a d33 piezoelectric charge coefficient from 7 pC N−1 to 9.9 pC N−1 . In terms of the d33, the PVDF sheets were suitable regardless of their Mw only after applying the elongation of 500%. Among all the investigated samples, those with an initial thickness of 1.0 mm did not seem to be suitable for vibration sensing purposes.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA19-17457S" target="_blank" >GA19-17457S: Výroba a analýza flexibilních piezoelektrických vrstev pro chytré strojírenství</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nanomaterials

ISSN

2079-4991

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

000676299600001

EID výsledku v databázi Scopus

2-s2.0-85108235116